Effect of sintering process parameters on the properties of 3Y-PSZ ceramics
نویسندگان
چکیده
The effect of sintering process parameters on the properties of 3 mol% yttria partially stability zirconia (3Y-PSZ) ceramics has been investigated. The relative density of the sintered pellet rapidly increases from 70.5 to 93.6 % with rose temperature from 1473 to 1573 K. In addition, the relative density only slightly increases from 94.9 to 96.6 %, when rose sintered temperature from 1573 to 1773 K. This result shows that no significant influence on the densification behavior when sintering at 1573 to 1773 K for 2 h. The Vickers hardness and toughness also increase with the sintered temperature.
منابع مشابه
Effect of Calcination Kinetics and Microwave Sintering Parameters on Dielectric and Peizo-Electric Properties of(K0.5Na0.5) NBO3 Ceramics
An efficient solid-state approach was established to synthesize (K0.5Na0.5) NbO3 ceramics using calcination kinetics and microwave assisted sintering. Milling of carbonate and oxide raw materials were carried out for 15h to obtain homogeneous nano particles. The crystallite size of 5.30 nm was obtained for the KNN system after calcination through optimized parameters and observed to be stoichio...
متن کاملBonding of TRIP-Steel/Al2O3-(3Y)-TZP Composites and (3Y)-TZP Ceramic by a Spark Plasma Sintering (SPS) Apparatus
A combination of the high damage tolerance of TRIP-steel and the extremely low thermal conductivity of partially stabilized zirconia (PSZ) can provide controlled thermal-mechanical properties to sandwich-shaped composite specimens comprising these materials. Sintering the (TRIP-steel-PSZ)/PSZ sandwich in a single step is very difficult due to differences in the sintering temperature and densifi...
متن کاملCold Sintering Process: New sintering technique for fabrication of nano-structured ceramics below 300 °C - A review
Due to the conventional understanding of sintering phenomenon in ceramic materials, considering two words of “cold” and “sintering” together may arise a doubt to a ceramic engineer since the usual sintering process has been accompanied by a heating regime at elevated temperatures. Recently, a new technique called Cold Sintering Process (CSP) has been introduced and developed as an ultra-low tem...
متن کاملGelcasting as a Novel Processing Route to Fabricate Partially Stabilized Zirconia Ceramic Bodies
Bioinert ceramics, like alumina and zirconia are used mainly for replacements of bones, hip joints and for dental implants. Partially stabilized zirconia ceramics (PSZ or TZP with 3 mol.% or 5 wt.% Y2O3), appear as perspective bioinert ceramics because of their high strength and corrosion resistance. In order to fabricate complex shapes, it is essential to use a near ...
متن کاملEffect of Silicon Carbide and graphite additives on the pressureless Sintering mechanism and microstructural characteristics of Ultra-High Temperature ZrB2 Ceramics Composites
The effect of SiC content, additives, and process parameters on densification and microstructural properties of pressureless sintered ZrB2– (1–10 wt %) SiC particulate composites have been studied. The ZrB2–SiC composite powders mixed by Spex mixer with 1-2wt% C (added as graphite powder) and CMC have been cold-compacted and sintered in argon environment in the temperature range of 1800–2100ºC ...
متن کامل