Corrosion Tests of Steel Earthing Electrodes with Protective Coatings Made from Different Materials

نویسندگان

  • Marek Loboda
  • Robert Marciniak
چکیده

In the paper the methodology and test results of field and laboratory corrosion tests of steel earthing rods with zinc galvanized coatings and copperbonded coatings are described. The corrosion rate and level of corrosion damage of earthing rods with two different protective coatings have been compared as well some conclusions related to reliability and assessment of technical “life time” of steel earthing rods with protective coatings are formulated.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Interpretation of Electrochemical Noise Signals Arising from Symmetrical and Asymmetrical Electrodes Made of Polypyrrole Coated Mild Steel

This article applies the standard deviation of partial signal (SDPS) plots of electrochemical noise (EN) current signals originating from corrosion events on the symmetrical and asymmetrical electrodes made of uncoated and polypyrrole (PPy)-coated mild steel alloy in 4000 ppm NaCl+1000 ppm NaNO2 solution. Signal recording was performed after 30, 60, 90 min and 24 h from immersion...

متن کامل

Corrosion of Different Materials in Combustion Chamber of Yellow Phosphorus Tail Gas in Industrial Boiler

About 75% of yellow phosphorus produced in the world is from China, and Yunnan province produces 60% of that in China. Yellow phosphorus is mostly produced by electric furnace from phosphate minerals. Through this method, 2500-3000 Nm/t tail gas is emitted, which causes pollution of the atmosphere. The key composition of the tail gas contains 80%~95%CO. Due to the “3R” principle (reducing, reus...

متن کامل

Corrosion Behavior of Detonation Gun Sprayed Fe-Al Type Intermetallic Coating

The detonation gun sprayed Fe-Al type coatings as an alternative for austenitic valve steel, were investigated using two different methods of testing corrosion resistance. High temperature, 10-hour isothermal oxidation experiments at 550, 750, 950 and 1100 °C show differences in the oxidation behavior of Fe-Al type coatings under air atmosphere. The oxide layer ensures satisfying oxidation resi...

متن کامل

Influence of Multiple Coating and Heat Treatment Cycles on the Performance of Nano-TiO2 Coating in Protection of 316L Stainless Steel against Corrosion under UV Illumination and Dark Conditions

In this study nanosized TiO2coatings on the 316L stainless steel substrate were prepared by means of dip-coating technique in which thickness of the coating layer increased byrepeating the coating cycles in two different routes: (I) dipping and drying,respectively, were repeated one, three and five times and finally the dried coated sample was heat treated (single); (II) multiple heat treatment...

متن کامل

Hydrophobic and superhydrophobic coatings for corrosion protection of steel

Since metals in general, and steels in particular, are vital construction materials in our modern society, the corrosion protection of said materials is of great importance, both to ensure safety and to reduce costs associated to corrosion. Previously, chromium (VI) and other harmful substances were effectively used to provide corrosion protection to steel, but since their use was heavily regul...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2016