Resistance of grain boundary array to cleavage cracking in free-standing thin film
نویسندگان
چکیده
In a previous experimental study on free-standing silicon thin film, it was observed that cleavage front transmission across a through-thickness grain boundary could be considerably constrained by film surfaces. As a result, the boundary toughness was much lower than its bulk counterpart. In this study, inspired by the observation of crack front behaviors at triple grain boundary junctions, we perform a theoretical analysis on the fracture resistance of a regular grain boundary array in a thin film. The result indicates that as the cleavage front breaks down into a number of sections by the grain boundaries, the overall fracture resistance can be increased by nearly 60%. However, if the grain size is too small, the fracture resistance may decrease. The optimum grain size is around 1/5 to 1/4 of the film thickness. This finding provides a scientific basis for further experimental investigation on advanced processing techniques. 2008 Elsevier Ltd. All rights reserved.
منابع مشابه
Energy equilibrium of cleavage front transmission across a high-angle grain boundary in a free-standing silicon thin film
In this article, the crack growth driving force and the resistance to cleavage cracking associated with crack front transmission across a high-angle grain boundary in a silicon thin film are analyzed, and a closed-form solution of grain boundary toughness is obtained. It is noticed that the fracture resistance of the grain boundary is a function of the film thickness. This size effect is attrib...
متن کاملOn size effect of cleavage cracking in polycrystalline thin films
A crack trapping model is developed for the fracture resistance of high-angle grain boundaries in free-standing brittle thin films, based on which a new size effect is predicted. In addition to the crystallographic misorientations, the grain boundary toughness is also dependent on the film thickness, primarily due to the geometrically necessary crack front branching. 2007 Elsevier Ltd. All righ...
متن کاملResistance of through-thickness grain boundaries to cleavage cracking in silicon thin films
Through a set of microtensile experiments, it was discovered that the resistance of a free-standing polycrystalline silicon thin film to cleavage cracking is not a material constant. Rather, it is highly dependent on the film thickness. As the film thickness changes from 1 to 10 lm, the fracture resistance increases by 20–60%, which can be attributed to the nonuniform nature of the crack front ...
متن کاملSecondary cracking at grain boundaries in silicon thin films
In this article, we report irregular cleavage front transmission at grain boundaries in free-standing polysilicon thin films. When the orientations of two adjacent grains are correlated, the crack may bypass the boundary via a ‘‘tunneling’’ process. Similar behavior can also be achieved if the crack path curves in the grain-boundary-affected zone. Moreover, the separation of crack flanks can be...
متن کاملCleavage cracking across triple grain boundary junctions in freestanding silicon thin films
This article is focused on a fractography study of cleavage cracking at triple grain boundary junctions in freestanding silicon thin films. At a triple junction, as the crystallographic orientations of the two grains ahead of the crack are different by only a few degrees, the cleavage front advance becomes quite jerky. The crack first enters the grain of smaller boundary toughness and then turn...