Synthesis of gamma ferric oxide by direct thermal decomposition of ferrous carbonate
ثبت نشده
چکیده
Ferrous carbonate was precipitated from the reaction of ferrous sulfate and sodium carbonate in an aqueous medium. The precipitate was calcined at different~eating rates (2, 5 and 10 °C/min, respectively) up to 500°C and the iron oxides produced were found to be magnetic. X-ray diffraction studies indicated the presence of gamma ferric oxide as a major phase in all the cases. It was found that wet precipitates, faster heating rate and short residence time in the furnace produced gamma ferric oxides with better magnetic properties (coercivity of around 360 Oe and saturation magnetization of 64 emu/g). The effect of aging time of ferrous carbonate precipitates on the magnetic properties was also studied. © 2002 Elsevier Science B.V. All rights reserved.
منابع مشابه
Synthesis of Different Copper Oxide Nano-Structures From Direct Thermal Decomposition of Porous Copper(ΙΙ) Metal-Organic Framework Precursors
Copper oxide nanostructures have been successfully synthesized via one-step solid-state thermolysis of two metal-organic frameworks, [Cu3(btc)2] (1) and [Cu(tpa).(dmf)] (2), (btc = benzene-1,3,5-tricarboxylate, tpa = therephtalic acid = 1,4-benzendicarboxylic acid and dmf = dimethyl formamide) under air atmosphere at 400, 500, and 600°C. It has also been found that the reaction temperature pla...
متن کاملSynthesis of Chromium Oxide Nano Particles by Thermal Decomposition Method
Disclosed is a method of preparing pigmentary chromium oxide nano particles having 50 percent particle size less than about 100 nm. Preparation of nano chromium (III) oxide is investigated by thermal decomposition method. According to the disclosed method, a substantially dry solid composition of potassium dichromate and carbon active is heated in CO2 atmosphere to a temperature of about 60...
متن کاملSynthesis and Characterization of Iron Oxide Nanoparticles by Thermal Decomposition Method of Iron (III) Chelates
Magnetic iron oxide nanoparticles have numerous applications in the biomedical field. This paper reports the preparation and properties of iron oxide nanoparticles synthesised by thermal decomposition method from iron chelates. The iron oxide nanoparticles were characterized by FTIR, powder XRD, VSM, SEM and TEM techniques. FTIR and powder XRD studies show that iron oxide was fo...
متن کاملSynthesis and characterization of a Bi-Oxide nanoparticle ZnO/CuO by thermal decomposition of oxalate precursor method
In the present work, we report the synthesis of binary nano metal oxides such as Zinc /Copper Oxide via novel dry synthetic methods such as thermal decomposition of oxalate precursor. The synthesis route involves facile solid-phase mechanochemical activation of a physical mixture of simple copper/zinc salts and oxalic acid, followed by calcination of the as-ground oxalate precursors at 450◦C. X...
متن کاملCobalt oxide nanoparticles by solid-state thermal decomposition: Synthesis and characterization
In this study, mononuclear octahedral cobalt(III) Schiff base complex [CoL3], L = (5-bromo-2-hydroxybenzyl-2-furylmethyl)imine, was synthesized from the reaction of Co(NO3)2•6H2O and the Schiff base ligand L in methanol as solvent. It used as a new precursor to prepare spinel type cobalt oxide nanoparticles by a facile solid-state thermal decomposition. Controlling the temperature and time, Co3...
متن کامل