Influence of relative humidity on the carbonation of calcium hydroxide nanoparticles and the formation of calcium carbonate polymorphs

A consolidating product based on nanoparticles of slaked lime (Ca(OH)2) dispersed in isopropyl alcohol was exposed under different relative humidities (RH), 33%, 54%, 75% and 90% during 7, 14, 21 and 28 days. The characterization of the calcium hydroxide nanoparticles and the formed calcium carbonate polymorphs has been performed by Micro-Raman spectroscopy, Transmission Electron Microscopy (TEM) and Environmental Scanning Electron Microscopy (ESEM) with Energy Dispersive X-ray Spectroscopy (EDS) and X-ray Diffraction (XRD). Precipitation and transformation of calcium carbonate polymorphs strongly depends on the relative humidity (RH). Higher RH (75%-90% RH) gives rise to amorphous calcium carbonate and monohydrocalcite, calcite, aragonite and vaterite, faster carbonation and larger particles sizes compared to lower RH (33%-54% RH) that gives rise only to portlandite and vaterite, slower carbonation and smaller particle sizes.