Mössbauer spectroscopic study of iron–nickel nitrides thin films prepared by ion beam assisted deposition
نویسندگان
چکیده
In this paper we have shown the feasibility of ion beam assisted deposition to produce iron–nickel nitride thin films of various compositions. We have carried out their compositional and structural characterization by means of Rutherford backscattering spectroscopy (RBS), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and integral conversion electron Mössbauer spectroscopy (ICEMS). The results have shown that Ni is incorporated within the films and that the temperature of the substrate has a large influence both in the phase composition obtained as well as in the degree of crystallinity of the thin films produced.
منابع مشابه
Characterization of CrBN films deposited by ion beam assisted deposition
of CrBN films deposited by ion beam assisted deposition" (2002). This article reports on the growth and analysis of CrBN nanocrystalline materials using an ion beam assisted deposition process. In addition, this article addresses the utilization of spectroscopic ellipsometry for in situ analysis of ternary nitrides. Coatings, with a total thickness of 1.5 Ϯ0.2 m, were deposited at low temperat...
متن کاملComposition and bonding structure of boron nitride B1-xNx thin films grown by ion-beam assisted evaporation
We present a detailed study of B1-xNx (0<x<0.6) films synthesized at room temperature by N2 + ion-beam assisted evaporation of boron. The atom-ion ratio was related to the final boron concentration as determined by X-ray energy dispersive spectroscopy (XEDS), and to the bonding structure explored by infrared (IR) and X-ray absorption near-edge structure (XANES) spectroscopies. IR and XANES reve...
متن کاملInfluence of Ni Deposition and Subsequent N+ Ion Implantation at Different Implantation Energies on Nano-Structure and Corrosion Behavior of 316 Stainless Steels
Nickel films of 300 nm thickness were deposited by electron beam evaporation at room temperature on 316 stainless steels. Corrosion studies of Ni coated 316 SS have been performed after N+ ion implantation at different energies of 20, 40, 60 and 80 keV. The structure and surface morphology of the films were evaluated using X-ray diffraction (XRD), atomic force microscope (AFM) an...
متن کاملElectrical properties of boron nitride thin films grown by neutralized nitrogen ion assisted vapor deposition
Boron nitride ~BN! thin films ~containing mixed cBN/hBN phase! have been deposited on Si~100! substrates using neutralized nitrogen beam and electron beam evaporation of boron. All as-deposited BN films were p type with a room-temperature carrier concentration in the range of 5310 to 1310 cm. The Mg-doped BN films showed carrier concentrations in the range of 1.2 310 cm to 5.2310 cm when the Mg...
متن کاملEffect of Thickness on Structural and Morphological Properties of AlN Films Prepared Using Single Ion Beam Sputtering
Aluminum nitride (AlN) thin films have potential applications in microelectronic and optoelectronic devices. In this study, AlN thin films with different thicknesses were deposited on silicon substrate by single ion beam sputtering method. The X-ray diffraction (XRD) spectra revealed that the structure of films with thickness of - nm was amorphous, while the polycrystalline hexagonal AlN with a...
متن کامل