Formation of nanostructured metallic glass thin films upon sputtering
نویسندگان
چکیده
Morphology evolution of the multicomponent metallic glass film obtained by radio frequency (RF) magnetron sputtering was investigated in the present work. Two modes of metallic glass sputtering were distinguished: smooth film mode and clustered film mode. The sputtering parameters, which have the most influence on the sputtering modes, were determined. As a result, amorphous Ni-Nb thin films with a smooth surface and nanoglassy structure were deposited on silica float glass and Si substrates. The phase composition of the target appeared to have a significant influence on the chemical composition of the deposited amorphous thin film. The differences in charge transport and nanomechanical properties between the smooth and nanoglassy Ni-Nb film were also determined.
منابع مشابه
Effect of Thickness on Properties of Copper Thin Films Growth on Glass by DC Planar Magnetron Sputtering
Copper thin films with nano-scale structure have numerous applications in modern technology. In this work, Cu thin films with different thicknesses from 50–220 nm have been deposited on glass substrate by DC magnetron sputtering technique at room temperature in pure Ar gas. The sputtering time was considered in 4, 8, 12 and 16 min, respectively. The thickness effect on the structural, mo...
متن کاملThe Effect of Substrate on Structural and Electrical Properties of Cu3N Thin Film by DC Reactive Magnetron Sputtering
The aim of this paper is to study the effect of substrate on the Cu3N thin films. At first Cu3N thin films are prepared using DC magnetron sputtering system. Then structural properties, surface roughness, and electrical resistance are studied using X-ray diffraction (XRD), the atomic force microscope (AFM) and four-point probe techniques respectively. Finally, the results are investigated and c...
متن کاملInfluence of aging temperature on phase transformation and mechanical behavior of NiTi thin films deposited by magnetron sputtering technique
In this study, NiTi thin films were deposited on the glass and NaCl substrates by means of magnetron sputtering method. The influence of aging temperature, over the range 300-500 oC, on phase transformation and mechanical properties of the sputtered NiTi thin films were studied by differential scanning calorimetry (DSC) and nano-indentation assay, respectively. The DSC curves showed that the ag...
متن کاملNanostructured Zr-Pd Metallic Glass Thin Film for Biochemical Applications
Zr-Pd metallic glassy thin films with a hierarchical nano-scale structure, produced by magnetron sputtering of the Zr and Pd powder mixture, demonstrate a unique combination of physical and biochemical properties. Thermal stability of the nano-structured glassy samples, their resistance to oxidation in dry air and phase transformation behavior are discussed in the present work. These binary all...
متن کاملMechanical Properties and Microstructural Evolution of Ta/TaNx Double Layer Thin Films Deposited by Magnetron Sputtering
Crystalline tantalum thin films of about 500nm thickness were deposited on AISI 316L stainless steel substrate using magnetron sputtering. To investigate the nano-mechanical properties of tantalum films, deposition was performed at two temperatures (25°C and 200°C) on TaNx intermediate layer with different N2/Ar flow rate ratio from 0 to 30%. Nano-indentation was performed to obtain the mechani...
متن کامل