Effect of LPSO and SFs on microstructure evolution and mechanical properties of Mg-Gd-Y-Zn-Zr alloy
نویسندگان
چکیده
High performance Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr alloy with high strength and excellent ductility has been successfully developed by hot extrusion. The effect of plate-shaped long period stacking ordered (LPSO) phases and solute-segregated stacking faults (SFs) on the dynamically recrystallization (DRX) behavior was analyzed. The plate-shaped LPSO phases stimulate the DRX by particle stimulated nucleation mechanism, leading to higher DRX ratio and weaker basal texture. While for the alloy with dense fine SFs inside the original grains, discontinuous DRX initially occurs at the original grain boundaries, and the DRX is obviously restricted. Consequently, alloy containing dense SFs exhibits higher strength but lower ductility compared with alloy with plated-shaped LPSO phases.
منابع مشابه
Achieving High Strength and Good Ductility in As-Extruded Mg–Gd–Y–Zn Alloys by Ce Micro-Alloying
In this study, the effect of Ce additions on microstructure evolution of Mg-7Gd-3.5Y-0.3Zn (wt %) alloys during the casting, homogenization, aging and extrusion processing are investigated, and novel mechanical properties are also obtained. The results show that Ce addition promotes the formation of long period stacking ordered (LPSO) phases in the as-cast Mg-Gd-Y-Zn-Ce alloys. A high content o...
متن کاملBiodegradable Mg-Zn-Y alloys with long-period stacking ordered structure: optimization for mechanical properties.
To optimize the mechanical properties for biodegradable orthopedic implant, microstructures and tensile properties of Mg-Zn-Y alloys containing long period stacking ordered (LPSO) phase were investigated. For the as-cast Mg(100-3x)(Zn(1)Y(2))(x) (1 ≤ x ≤ 3) alloys, volume fraction of 18R LPSO phase increases with increasing the contents of Zn and Y. Mg(97)Zn(1)Y(2) alloy exhibits the optimal co...
متن کاملDeformation twinning induced decomposition of lamellar LPSO structure and its re-precipitation in an Mg-Zn-Y alloy
The high hardness or yield strength of an alloy is known to benefit from the presence of small-scale precipitation, whose hardening effect is extensively applied in various engineering materials. Stability of the precipitates is of critical importance in maintaining the high performance of a material under mechanical loading. The long period stacking ordered (LPSO) structures play an important ...
متن کاملEffect of Mechanical Alloying and Sintering on Phase Transformation, Microstructural Evolution, Mechanical Properties and Density of Zr-Cr Alloy
The purpose of present research was production ofZr-based alloy as the nuclear fuel cladding by mechanical alloying (MA) and sintering process. Firstly, Zr and Cr powders were mechanically alloyed to produce the refractory and hard Zr-10 wt% Cr alloy, and then, the powder mixtures were consolidated by press and following sintering at temperature of 800˚C min. The phase evolution, microstructura...
متن کاملProduction of Cu-Cr-Zr Alloy Using Electro Slag Remelting Technique (RESEARCH NOTE)
This study focused on the effect of electro slag remelting process (ESR) on microstructure and composition of an as-cast alloy of Cu-Cr-Zr. These observations revealed that applying ESR process results in a more uniform distribution of alloying elements, however a slight aggregation of large precipitates and inclusions existed in as-cast ingot was found. Additionally, impurities like P, S and M...
متن کامل