Deactivation Pattern of a “Model” Ni/MgO Catalyst in the Pre-Reforming of n-Hexane
نویسنده
چکیده
The deactivation pattern of a “model” Ni/MgO catalyst in the pre-reforming of n-hexane with steam (T, 450 °C; P, 5–15 bar) is reviewed. The influence of the steam-to-carbon ratio (S/C, 1.5–3.5) on the rate of catalyst fouling by coking is ascertained. Catalyst fouling leads to an exponential decay in activity, denoting 1-order dependence of the coking process on active sites availability. Hydrogen hinders the coking process, though slight activity decay is due to sintering of the active Ni phase. Deactivation by thiophene causes a sharp, almost linear, drop to nearly zero activity within only 6 h; this deactivation is likely due to dissociative adsorption of thiophene with subsequent strong, irreversible chemical adsorption of S-atoms on active Ni sites, i.e., irreversible poisoning. Modeling of activity decay curves (α, at/a0) by proper kinetic equations allows assessing the effects of temperature, pressure, S/C, H2 and thiophene feed on the deactivation pattern of the model Ni/MgO catalyst by coking, sintering, and poisoning phenomena.
منابع مشابه
Kinetic comparison of Ni/Al2O3 and Ni/MgO-Al2O3 nano structure catalysts in CO2 reforming of methane
The kinetic characteristics of the Ni/Al2O3 and Ni/MgO-Al2O3 catalysts were investigated in CO2 reforming of methane (CRM). The reaction orders (α and β) and the rate constant (k) were calculated using the non-linear regression analysis, in which the sum of the squared differences of calculated and experimental CO2 reforming of m...
متن کاملAn Investigation into the Effect of Hydrotalcite Calcination Temperature on the Catalytic Performance of Mesoporous Ni-MgO-Al2O3 Catalyst in the Combined Steam and Dry Reforming of Methane
Several mesoporous nickel-based catalysts with MgO-Al2O3 as the catalyst support were prepared using a co-precipitation method at a constant pH. The supports were prepared from the decomposition of an Mg-Al hydrotalcite-like structure which had already been prepared with Mg/Al=1. Prior to impregnating 10 wt.% nickel on the supports, the precursor was decomposed at several ...
متن کاملSignificantly Improved Catalytic Performance of Ni-Based MgO Catalyst in Steam Reforming of Phenol by Inducing Mesostructure
A Ni/meso-MgO catalyst with high surface area and small Ni nanoparticles was synthesized and investigated for hydrogen production by steam reforming of phenol for the first time. Compared to conventional Ni/MgO, the Ni/meso-MgO catalyst showed higher catalytic activity and stability. X-ray Diffraction, N2 adsorption, hydrogen temperature programmed reduction, transmission electron microscopy an...
متن کاملOptimization of the preparation procedure of Ni/Al2O3 catalyst for steam reforming of n-butane
Performance of Ni/Al2O3 catalysts (10 wt.% Ni) in steam reforming of n-butane was investigated in terms of n-butane conversion, selectivity to hydrogen and hydrogen yield. The process was carried out in a fixed-bed tubular reactor at 650 °C and atmospheric pressure. The volumetric flow rates of n-butane and steam were 0.1 mL/min and 0.6 mL/min, respectively. The catalysts were prepared by preci...
متن کاملStable Hydrogen Production from Ethanol through Steam Reforming Reaction over Nickel-Containing Smectite-Derived Catalyst
Hydrogen production through steam reforming of ethanol was investigated with conventional supported nickel catalysts and a Ni-containing smectite-derived catalyst. The former is initially active, but significant catalyst deactivation occurs during the reaction due to carbon deposition. Side reactions of the decomposition of CO and CH4 are the main reason for the catalyst deactivation, and these...
متن کامل