The Wear Resistance of Cryogenically Treated Diamond-Like Carbon Films
نویسندگان
چکیده
This study explored the effects of cryogenic treatment on the microstructure, hardness, and wear-resistance of diamond-like carbon (DLC) by cryogenically treating NAK 80 mold steel coated with DLC. Raman spectroscopy analyzed the structure of the DLC film. Nanoindenter analyzed the hardness and Young’s modulus of the film, and their relationship determined the wear resistance. Wear test assessed the wear rate and friction coefficient of the DLC film. The results showed that cryogenic treatment increased the rate of carbide precipitation and refined the grain structure. Raman spectroscopy indicated that the Raman intensity rate (ID/IG) of treated DLC films was smaller than those without cryogenic treatment. When the sp3 bond increased, the hardness and wearresistance of the DLC film also increased.
منابع مشابه
Influence of carbon sputtering power on structure, corrosion resistance, adhesion strength and wear resistance of platinum/ruthenium/nitrogen doped diamond-like carbon thin films
متن کامل
Investigation of structure, adhesion strength, wear performance and corrosion behavior of platinum/ruthenium/nitrogen doped diamond-like carbon thin films with respect to film thickness
In this study, the corrosion performance of platinum/ruthenium/nitrogen doped diamond-like carbon (PtRuN-DLC) thin films deposited on p-Si substrates using a DCmagnetron sputtering deposition system in a 0.1M NaCl solution was investigated using potentiodynamic polarization test in terms of film thickness. Theeffect of thefilmthickness on the chemical composition, bonding structure, surfacemorp...
متن کاملEffect of Catalyst on the Growth of Diamond-like Carbon by HFCVD
Diamond like carbon (DLC) film was grown by hot filament chemical vapor deposition (HFCVD)technique. In the present work, we investigated the quality of the DLC films groew on the substratesthat were coated with various metal nanocatalysts (Au and Ni). A combination of CH4/Ar/H2 rendersthe growth of carbon nanostructures technique (diamond like carbon). The utilized samples werecharacterized by...
متن کاملDeposition of DLC/oxynitriding Films onto JIS SKD11 Steel by Bipolar-pulsed PECVD
Traditionally, JIS SKD11 tool steel is corresponding to the AISI D2. Since this material possesses high hardness and excellent wear resistance, it is usually used as a mold material and cutting tools.1,2) In order to improve the tool life, many studies have focused on surface treatment as a method of protecting the internal material.2) Nitriding is a thermo-chemical process with nitrogen diffus...
متن کاملCharacterization of diamond-like carbon films deposited on commercially pure Ti and Ti–6Al–4V
The diamond-like carbon (DLC) films deposited on the articulating surface of medical-grade Ti and Ti–6Al–4V were characterized. The DLC films were synthesized by r.f. plasma assisted chemical vapor deposition (PACVD) using C6H6 at 10 mTorr. For wear tests, the ball-ondisk type wear tester was employed by wearing a 5-mm diameter ruby ball against a rotating metal disk. The DLC coating dramatical...
متن کامل