Overload effects on the fatigue crack propagation behaviour in Inconel 718
نویسنده
چکیده
In this master thesis, work done in the TURBO POWER project High temperature fatigue crack propagation in nickel-based superalloys during spring 2012 will be presented. The overall objective of this project is to develop and evaluate tools for designing against fatigue in gas turbine applications, with special focus on the crack propagation in the nickel-based superalloy Inconel 718. Experiments have been performed to study the effect of initial overloads, and it has been shown that even for small initial overloads a significant reduction of the crack growth rate is received. Furthermore, FE simulations have been carried out in order to describe the local stress state in front of the crack tip since it is believed to control, at least partly the diffusion of oxygen into the crack tip and thus also the hold time crack growth behaviour of the material. Finally, an evaluation method for the stresses is presented, where the results are averaged over an identifiable process/damaged zone in front of the crack tip.
منابع مشابه
High temperature fatigue crack propagation behaviour of Inconel 718
The overall objective of this work has been to develop and evaluate tools for designing against fatigue in gas turbine applications, with special focus on the nickelbased superalloy Inconel 718. The fatigue crack propagation behaviour under high temperature hold times has been studied. Firstly, the main fatigue crack propagation phenomena have been investigated with the aim of setting up a basi...
متن کاملConstitutive and fatigue crack propagation behaviour of Inconel 718
In this licentiate thesis the work done in the TURBO POWER project Influence of high temperature hold times on the fatigue life of nickel-based superalloys will be presented. The overall objective of this project is to develop and evaluate tools for designing against fatigue in gas turbine applications, with special focus on the nickel-based superalloy Inconel 718. Firstly, the constitutive beh...
متن کاملHold-time effect on the thermo-mechanical fatigue crack growth behaviour of Inconel 718
In-phase TMF crack growth testing with different lengths of the hold time at the maximum temperature of 550C has been conducted on Inconel 718 specimens. Focus has been on establishing a method for TMF crack growth testing and investigating the effect of high temperature hold times on the TMF crack growth of the material. The tests are compared to isothermal crack propagation tests and show go...
متن کاملModelling of fatigue crack propagation in Inconel 718 under hold time conditions
In this thesis an investigation and modelling of the fatigue crack propagation in the nickel based superalloy Inconel 718, with a special emphasis on the effect of hold times, is presented. The modelling work has been concentrated on describing the hold time fatigue crack propagation by using the concept of a damaged zone in front of the crack tip, which is believed to have a lowered resistance...
متن کامل