Nanoporous Pd (np-Pd) was prepared by co-sputtering Pd-Ni alloy films onto Si substrates, followed by chemical dealloying with sulfuric acid. X-ray diffractometry and chemical analysis were used to track the extent of dealloying. The np-Pd structure was changed from particle-like to sponge-like by diluting the sulfuric acid etchant. Using suitable precursor alloy composition and dealloying conditions, np-Pd films were prepared with uniform and open sponge-like structures, with interconnected ligaments and no cracks, yielding a large amount of surface area for reactions with hydrogen. Np-Pd films exhibited shorter response time for hydrogen absorption/desorption than dense Pd films, showing promise for hydrogen sensing.
منابع مشابه
Changes in crystallographic orientation of thin foils of palladium and palladium alloys after the absorption of hydrogen
The adsorption/absorption of hydrogen at room temperature by palladium, 16% silver-palladium and 5% ruthenium-palladium foils was studied using thermal desorption spectroscopy. Hydrogen readily diffused in the palladium and desorbed as one broad peak at about 650 K. Hydrogen also diffuses in the 16% silver-palladium foil and in the 5% rutheniumpalladium foil but with a smaller diffusion constan...
متن کاملDevelopment of Palladium-Alloy Membranes for Hydrogen Separation and Purification
This paper summarizes R&D activities and progress at NORAM Engineering and the University of British Columbia (UBC) on preparation and testing of thin palladium-based membranes and their applications. Most of these activities were carried out internally at NORAM, some jointly with UBC and their spin-off company, Membrane Reactor Technology (MRT) through a wide range of projects. Key results out...
متن کاملStudy of Composition and Optical Properties of Chemically Deposited Pd-xSb2S3 Thin Films
The study reports on the effects of different concentration of palladium impurities on the compositional and optical properties of Palladium Doped Antimony Sulphide (Pd-xSb2S3) thin films grown by the chemical bath deposition method. The films were grown at room temperature and other deposition conditions such as the bath temperature, pH, complexing agents were kept constant. The concentration ...
متن کاملPreparation of Graphene-amine Nanofluid for Absorption of Carbon Dioxide (CO2) and Hydrogen Sulfide (H2S) from a Natural Gas Stream in a Wetted Wall Column
In this study, it was shown that how CO2 and H2S were removed from a natural gas stream, using a nanofluid containing nanoporous graphene in Diehanolamine (DEA). Before running the experiments, the appropriate values were chosen for the nanosheet dosage and the liquid and gas flow rates in the absorption experiments, which were performed in a laboratory scale wetted wall column. In the expe...
متن کاملبررسی قابلیت جذب هیدروژن در ماده مرکب نانوساختار SBA-16-Pd
The purpose of this work was to study the hydrogen adsorption on the surface of mesoporous materials based on silica (SBA-16) modified with palladium via temperature. Since mesoporous silica materials have a high specific surface area, and the ordered mesoporous size of 2-10nm, they are suitable for adsorption and storage of hydrogen. SBA-16 is suitable for this purpose due to its cubic crystal...