Iron supplementation reduces the erosive potential of a cola drink on enamel and dentin in situ

UNLABELLED Iron has been suggested to reduce the erosive potential of cola drinks in vitro. OBJECTIVE The aim of this study was to evaluate in situ the effect of ferrous sulfate supplementation on the inhibition of the erosion caused by a cola drink. MATERIAL AND METHODS Ten adult volunteers participated in a crossover protocol conducted in two phases of 5 days, separated by a washout period of 7 days. In each phase, they wore palatal devices containing two human enamel and two human dentin blocks. The volunteers immersed the devices for 5 min in 150 mL of cola drink (Coca-ColaTM, pH 2.6), containing ferrous sulfate (10 mmol/L) or not (control), 4 times per day. The effect of ferrous sulfate on the inhibition of erosion was evaluated by profilometry (wear). Data were analyzed by paired t tests (p<0.05). RESULTS The mean wear (±se) was significantly reduced in the presence of ferrous sulfate, both for enamel (control: 5.8±1.0 µm; ferrous sulfate: 2.8±0.6 µm) and dentin (control: 4.8±0.8 µm; ferrous sulfate: 1.7±0.7 µm). CONCLUSIONS The supplementation of cola drinks with ferrous sulfate can be a good alternative for the reduction of their erosive potential. Additional studies should be done to test if lower ferrous sulfate concentrations can also have a protective effect as well as the combination of ferrous sulfate with other ions.