Demineralized dentin 3D porosity and pore size distribution using mercury porosimetry.

نویسندگان

  • Elsa Vennat
  • Christine Bogicevic
  • Jean-Marie Fleureau
  • Michel Degrange
چکیده

OBJECTIVES The objectives of this study were to assess demineralized dentin porosity and quantify the different porous features distribution within the material using mercury intrusion porosimetry (MIP) technique. We compared hexamethyldisilazane (HMDS) drying and lyophilization (LYO) (freeze-drying) in sample preparation. METHODS Fifty-six dentin discs were assigned into three groups. The control (CTR) group discs were superficially acid-etched (15s 37% H(3)PO(4)) to remove the smear layer and then freeze-dried whereas LYO and HMDS groups samples were first totally demineralized using EDTA 0.5M and then freeze-dried and HMDS-dried respectively. MIP was used to determine open porosity and pore size distribution of each pair of samples. Field emission scanning electron microscopy (FESEM) was used to illustrate the results. RESULTS The results showed two types of pores corresponding either to tubules and micro-branches or to inter-fibrillar spaces created by demineralization. Global porosity varied from 59% (HMDS-dried samples) to 70% (freeze-dried samples). Lyophilization drying technique seems to lead to less shrinkage than HMDS drying. FESEM revealed that collagen fibers of demineralized lyophilized samples are less melted together than in the HMDS-dried samples. SIGNIFICANCE Demineralized dentin porosity is a key parameter in dentin bonding that will influence the hybrid layer quality. Its characterization could be helpful to improve the monomers infiltration.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Pore size distribution in tablets measured with a morphological sieve.

Porosity and pore structure are important characteristics of tablets, since they influence mechanical strength and many other properties. This paper proposes an alternative method for the characterization of pore structure based on image analysis of SEM micrographs. SEM images were made of sodium chloride tablets made with three different particle sizes. The pore size distribution in these imag...

متن کامل

Investigation and Computer Modellin . G of the Pore Structure of Paper and of Consolidated Pigment Coatings

The aim of this project was to enhance the current state of knowledge of the void structure of paper, and pigments used to coat paper. The porosities and pore size distributions of consolidated pigments were measured using mercury porosimetry. Prior to this work, mercury porosimetry was rarely used in this field due to problems associated with the conventional interpretation of mercury porosime...

متن کامل

Characterization of the Compaction and Sintering of Hydroxyapatite Powders by Mercury Porosimetry*

Pvlercury porosimetry was used to measure the bulk and real densities, pore volumes and pore size distributions of compacts of hydroxyapatite before and after sintering. The hydroxyapatites were prepared by two different methods and had widely different surface areas. The properties were determined as a function of compaction force and sintering temperature. Densities from porosimetry were in g...

متن کامل

Use of Mercury Porosimetry and Nitrogen Adsorption in Characterisation of the Pore Structure of Mannitol and Microcrystalline Cellulose Powders, Granules and Tablets

USE OF MERCURY POROSIMETRY AND NITROGEN ADSORPTION IN CHARACTERISATION OF THE PORE STRUCTURE OF MANNITOL AND MICROCRYSTALLINE CELLULOSE POWDERS, GRANULES AND TABLETS Sari Westermarck, 2000, University of Helsinki (FIN), pp. 50. ISBN952-91-2534-8 The effects of pretreatment and scanning speed of mercury porosimetry on the mercury porosimetry results of non-hygroscopic mannitol and hygroscopic mi...

متن کامل

Analysis of Wood Pore Characteristics with Mercury Intrusion Porosimetry and X-ray Micro- Computed Tomography

The size and distribution of wood pores greatly influence its properties like density, thermal conductivity and permeability as well as acoustical property. Different techniques were developed to measure wood pore characteristic parameters. In this paper, mercury intrusion porosimetry (MIP) and X-ray Micro-computed tomography (μCT) were used to characterize pore characteristics of Populus L. wo...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Dental materials : official publication of the Academy of Dental Materials

دوره 25 6  شماره 

صفحات  -

تاریخ انتشار 2009