Effect of Loading Rate on Dynamic Fracture Morphology of a Zr-Based Bulk Metallic Glass
نویسندگان
چکیده
Low-velocity plate impact experiments using a single-stage gas-gun are performed on Zr58.5Cu15.6Ni12.8Al10.3Nb2.8. Compressive fracture surfaces of the samples subjected to varying impact velocities and stress amplitudes are evaluated in order to study their loading rate dependence. Samples impacted at increasing loading rates, from increasing velocities of impact, show a larger extent of localized melting while those subjected to increasing stress show a transition from ductile to brittle fracture. These observations suggest that the mechanisms and morphology of fracture are strain-rate dependent. [doi:10.2320/matertrans.M2014467]
منابع مشابه
Fracture behavior of Zr55Cu30Al10Ni5 bulk metallic glass under quasi-static and dynamic compression
Fracture behavior of Zr55Cu30Al10Ni5 bulk metallic glass was investigated under quasi-static compression at strain rate of 10/s using an Instron testing machine and dynamic split Hopkinson bar (SHPB) compression with strain rate of about 1900–4300/s. Pronounced strain softening, especially past the peak stress, was observed under SHPB tests and compared with the distinct flow serrations under q...
متن کاملFracture behaviors under pure shear loading in bulk metallic glasses
Pure shear fracture test, as a special mechanical means, had been carried out extensively to obtain the critical information for traditional metallic crystalline materials and rocks, such as the intrinsic deformation behavior and fracture mechanism. However, for bulk metallic glasses (BMGs), the pure shear fracture behaviors have not been investigated systematically due to the lack of a suitabl...
متن کاملMicrostructure controlled shear band pattern formation and enhanced plasticity of bulk metallic glasses containing in situ formed ductile phase dendrite dispersions
Results are presented for a ductile metal reinforced bulk metallic glass matrix composite based on glass forming compositions in the Zr-Ti-Cu-Ni-Be system. Primary dendrite growth and solute partitioning in the molten state yields a microstructure consisting of a ductile crystalline Ti-Zr-Nb beta phase, with bcc structure, in a Zr-Ti-Nb-Cu-Ni-Be bulk metallic glass matrix. Under unconstrained m...
متن کاملFracture Toughness Study on Bulk Metallic Glasses and Novel Joining Method Using Bulk Metallic Glass Solder
The fracture toughness of three new compositional variants of the Zr-Ti-Be-LTM (Late Transition Metal) family of bulk metallic glasses (BMG’s) are studied in the as-cast and annealed condition. Quaternary Zr-Ti-Cu-Be alloys consistently had linear elastic fracture toughness values greater than 80 MPa·m, while Vitreloy 1, a Zr-Ti-Cu-Ni-Be alloy, had an average fracture toughness of 48.5 MPa·m wi...
متن کاملReduced Fracture Toughness of Metallic Glass at Cryogenic Temperature
The effects of cryogenic temperature on the toughness of a Zr-based metallic glass are investigated. Based on three-dimensional fracture morphologies at different temperatures, the crack formation and propagation are analyzed. Through the calculation of the shear transformation zone volume, the shear modulus and bulk modulus of the metallic glass at different temperatures and the crack formatio...
متن کامل