Oxidation Performance of Platinum-Clad Mo-47Re Alloy
نویسندگان
چکیده
The alloy Mo-47Re has favorable mechanical properties at temperatures above 1400 C, but it undergoes severe oxidation when used in air with no protective coating. To shield the alloy from oxidation, platinum cladding has been evaluated. The unprotected alloy undergoes catastrophic oxidation under static and dynamic oxidation conditions. The platinum cladding provides good protection from static and dynamic oxidation for moderate times at 1260 C. Samples tested for longer times under static oxidation conditions experienced severe oxidation. The data suggest that oxidation results from the transport of oxygen through the grain boundaries and through the pinhole defects of the platinum cladding.
منابع مشابه
High Temperature Erosion- Oxidation Behavior of Nickel- Based Alloys Containing Mo in Fluidized Bed Waste Incineration
High-temperature erosion-oxidation behavior of nickel-based alloys containing 0-7 wt.% Mo in fluidized bed waste incineration conditions was studied. A stream of hot condensed air with a flow rate of 25 L/min caused hot silica sand (700 °C) mixed with 0.5 wt.% of chloride salts to hit the specimens for 250 h. By removing the erosive factor, the high-temperature oxidation behavior of the alloys ...
متن کاملIridium-platinum alloy nanoparticles: Composition-dependent electrocatalytic activity for formic acid oxidation†
IrxPt100 x alloy nanoparticles with varied compositions (x1⁄4 100, 75, 67, 50, 34, and 0) were synthesized by a thermolytic process at varied ratios of the IrCl3 and PtCl2 precursors. High-resolution transmission electron microscopic (HRTEM) measurements showed that the nanoparticles all exhibited well-defined crystalline structures with the average core diameters around 2 nm; and the elemental...
متن کاملارزیابی مقاومت به اکسایش پیوسته پوشش پاشش حرارتی Mo-Si-B روی فولاد ساده کربنی
In this study, Mo-14Si-10B and Mo-57Si-10B (at%) elemental powders were separately milled using an attritor mill. Mechanically alloyed powders were agglomerated and annealed. Then, powders of Mo-Si-B as alloyed (with composites) and agglomerated (without composites) were plasma sprayed onto plain carbon steels. The samples, both coated and non-coated, were subjected to isothermal oxidation test...
متن کاملV2o5-mwnt Nanocomposite as a Promising Support for Platinium in Methanol Electro - Oxidation
Introduction Direct methanol fuel cells are very important as a clean, low cost and portable power source because of several environmental problems in traditional energy producing systems. Compared to the hydrogen fueled PEMFCs, direct methanol PEMFCs are more compact and can be used in power portable electric devices. Platinum is the most active electro-catalyst for the electro-oxidation of me...
متن کاملElectrosynthesized Reduced Graphene Oxide-Supported Platinum, Platinum-Copper and Platinum-Nickel Nanoparticles on Carbon-Ceramic Electrode for Electrocatalytic Oxidation of Ethanol in Acidic Media
In this work, the electrocatalytic oxidation of ethanol was studied in acidic media at the wholly electrosynthesized nanocomposites: platinum and its alloys (copper and nickel) anoparticles/reduced graphene oxide on the carbon-ceramic electrode (Pt/rGO/CCE, Pt-Cu/rGO/CCE, and Pt-Ni/rGO/CCE electrocatalysts). The electrosynthesized nanocomposites were characterized by scan...
متن کامل