Dielectric properties of polypropylene fabrics with carbon plasma coatings for applications in the technique of electromagnetic field shielding
نویسندگان
چکیده
Within the current work an attempt was made to use glow discharge low temperature plasma processing to produce carbon coatings on polypropylene unwoven fabric for electromagnetic field shielding applications. Layers were obtained from the gaseous phase (propane–butane). The influence of coatings on the dielectric buffer properties of modified fabrics was investigated. The Havriliak–Negami (HN) function precisely fits our relaxation data, hence the HN parameters could be used to control and optimize the processing of plasma coatings. The method of obtaining conducting layers requires further research. 2010 Elsevier B.V. All rights reserved.
منابع مشابه
Mechanical Properties of Polypropylene Coating Containing Maleic Anhydride on Plain Carbon Steel
Using Electrostatic Spray Coating Technique, Polypropylene Powder (EPD 60R) was applied on carbon steel substrates at room temperature. In order to obtain a uniform coating, steel substrates with powder coatings were heated in a vacuum oven at various temperatures up to 250° C for various periods of time up to 45 min and a pressure of 200 mb. The coatings produced had thicknesses of around 470 ...
متن کاملMechanical Properties of Polypropylene Coating Containing Maleic Anhydride on Plain Carbon Steel
Using Electrostatic Spray Coating Technique, Polypropylene Powder (EPD 60R) was applied on carbon steel substrates at room temperature. In order to obtain a uniform coating, steel substrates with powder coatings were heated in a vacuum oven at various temperatures up to 250° C for various periods of time up to 45 min and a pressure of 200 mb. The coatings produced had thicknesses of around 470 ...
متن کاملDielectric Strontium Zirconate Sprayed by a Plasma Torch
Amultifunctional material, strontium zirconate, SrZrO3, studied in literatures as a dielectric ceramics, thermal barrier coating, proton-conductor, and luminescent material was sprayed by a water-stabilized plasma torch WSP 500. Stainless steel and plain carbon steel were used as substrates. Coatings with thickness of 1 to 2 mm were produced, whereas the substrates were preheated over 450 °C. T...
متن کاملEffect of carbon black content on the microwave absorbing properties of CB/epoxy composites
To prevent serious electromagnetic interference, a single-layer and double layer wave-absorbing coating employing complex absorbents composed of carbon black with epoxy resin as matrix was prepared. The morphologies of carbon black /epoxy composites were characterized by scanning electron microscope and atomic force microscope, respectively. The carbon black particles exhibit obvious polyarom...
متن کاملDielectric properties of plasma sprayed silicates subjected to additional annealing
Several silicate materials were plasma sprayed and characterized by the authors in recent years from the point of view of their chemical and phase compositions, microstructure and mechanical as well as thermal properties. Present work is concerned with selected dielectric properties of these deposits. Synthetic mullite and steatite as well as natural olivine-forsterite were plasma sprayed using...