Effect of Grinding and Resintering on the Fatigue Limit and Surface Characterization of a Y-TZP Ceramic.

نویسندگان

  • Gabriela Scatimburgo Polli
  • Gabriel Rodrigues Hatanaka
  • Filipe de Oliveira Abi-Rached
  • Lígia Antunes Pereira Pinelli
  • Márcio de Sousa Góes
  • Paulo Francisco Cesar
  • José Maurício Dos Santos Nunes Reis
چکیده

This study evaluated the effect of grinding protocols and resintering on flexural fatigue limit and surface characterization of LavaTM Y-TZP. Bar-shaped specimens (20×4.0×1.2 mm, n=40; 20×4.0×1.5 mm, n=80) were obtained. Half of the thinner specimens (1.2 mm) constituted the as-sintered group (AS), while the thicker ones (1.5 mm) were ground with diamond burs under irrigation (WG) or not (G). The other half of thinner and half of ground specimens were resintered (1000 ºC, 30 min), forming the groups ASR, WGR and GR. Fatigue limit (500,000 cycles, 10 Hz) was evaluated by staircase method in a 4-point flexural fixture. Data were analyzed by 2-way ANOVA and Tukey's test (α=0.05). Surface topography (n=3) and fracture area (n=3) were evaluated by SEM. X-ray diffraction data (n=1) was analyzed by Rietveld refinement. ANOVA revealed significant differences (p<0.001) for the grinding protocol, resintering and their interaction. Grinding increased the fatigue limit of non-resintered groups. There was no significant difference among the resintered groups. Resintering significantly increased the fatigue limit of the AS group only. Both protocols created evident grooves on zirconia surface. The failures initiated at the tensile side of all specimens. The percentages (wt%) of monoclinic phase were AS (8.6), ASR (1.2), G (1.8), GR (0.0), WG (8.2), WGR (0.0) before, and AS (7.4), ASR (6.5), G (3.2), GR (0.2), WG (4.6), WGR (1.1) after cyclic loading. Grinding increased the fatigue limit of non-resintered Y-TZP and formed evident grooves on its surface. Resintering provided significant increase in the fatigue limit of as-sintered specimens. In general, grinding and resintering decreased or zeroed the monoclinic phase.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of Alumina Addition to Zirconia Nano-composite on Low Temperature Degradation Process and Biaxial Strength

Ceramic dental materials have been considered as alternatives to metals for dental implants application. In this respect, zirconia tetragonal stabilized with %3 yttrium, is of great importance among the ceramic materials for endosseous dental implant application. Because of its good mechanical properties and color similar to tooth. The aim and novelty of this study was to design and prepare Y-T...

متن کامل

Plasticity 4 nduced Fatigue Damage in Ceria - Stabil

Current studies on the fatigue lifetime of ceramics are mostly focused on the relation between the stress amplitude (or maximum stress) and cycles to failure. For a more compliant and plastic ceramic which has a pronounced nonlinear stress-strain relation, the role of plastic strain in the fatigue damage is investigated for the first time in this study using a 12 mol% Ce-TZP. By testing at diff...

متن کامل

Gelcasting as a Novel Processing Route to Fabricate Partially Stabilized Zirconia Ceramic Bodies

     Bioinert ceramics, like alumina and zirconia are used mainly for replacements of bones, hip joints and for dental implants. Partially stabilized zirconia ceramics (PSZ or TZP with 3 mol.% or 5 wt.% Y2O3), appear as perspective bioinert ceramics because of their high strength and corrosion resistance. In order to fabricate complex shapes, it is essential to use a near ...

متن کامل

Fatigue sensitivity of Y-TZP to microscale sharp-contact flaws.

The strength degrading effects of sharp-contact damage are examined for Y-TZP ceramic plates bonded to a plastic substrate. Contacts are made with Vickers and Berkovich diamond indenters at low loads (0.1 N to 100 N) in the ceramic lower surfaces prior to bonding to the substrates. The indentations remain in the subthreshold region, that is, without visible corner radial cracks, over the lower ...

متن کامل

Effects of Various Chairside Surface Treatments on Zirconia-Resin Cement Bond Strength

Introduction: Various surface treatments have been used to improve the adhesion of resin cement to zirconia restorations. The present study aimed to investigate the effects of different surface treatments on the bond strength of resin cement to zirconia (Y-TZP) in clinical practice. Methods: thirty square Y-TZP samples were classified into three groups of 10, including group SB (50 µm sandblast...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Brazilian dental journal

دوره 27 4  شماره 

صفحات  -

تاریخ انتشار 2016