Effect of Mean Stress on Fatigue Crack Growth Behavior of Stainless Steel 304L
نویسندگان
چکیده
Stainless steel has been employed in many engineering applications ranging from pharmaceutical equipment to piping in the nuclear reactors and storage to chemical products. In this attempt, simulation of fatigue crack growth based on experimental results of austenitic stainless steel 304L was presented using AFGROW code when NASGRO mode laws adopted. Double through crack at hole specimen is used in this investigation under constant amplitude loading. Effect of mean stress is highlighted. Results show that fatigue crack growth rate (FCGR) and fatigue life were affected by maximum applied load and dimension of hole. An equivalent of Paris law for this material was estimated. Keywords—Fatigue crack, stainless steel, mean stress, amplitude loading.
منابع مشابه
constant-amplitude experiments show a sensitivity of the crack growth rate to the R-ratio and the effect of amplitude loading
Stainless steel has been employed in many engineering applications ranging from pharmaceutical equipment to piping in the nuclear reactors and storage to chemical products. In this attempt, simulation of fatigue crack growth based on experimental results of austenitic stainless steel 304L was presented using AFGROW code when NASGRO mode laws adopted. Double through crack at hole specimen is use...
متن کاملFull field measurements of anisotropic stress intensity factor ranges in fatigue
The effects of anisotropy during mixed mode fatigue crack growth were studied in single crystal 316L stainless steel. An anisotropic least-squares regression algorithm using displacements from digital image correlation was developed to find the effective stress intensity factors, KI and KII, and the T-stress. Crack tip plastic zones were determined using an anisotropic yield criterion. Strains ...
متن کاملEffect of Grain Size on Collective Damage of Short Cracks and Fatigue Life Estimation for a Stainless Steel
In the short crack regime of the fatigue process, grain boundaries in steels are barriers against crack growth. In this paper, we use: (1) a method involving crack density; and (2) a method of dimensional analysis, to evaluate the effects of grain size and grain-boundary resistance on short crack behaviour and fatigue life. The results show that the fatigue life increases with a decrease in gra...
متن کاملBiaxial High Cycle Fatigue of a Type 304L Stainless Steel: Cyclic Strains and Crack Initiation Detection by Digital Image Correlation
A series of biaxial High Cycle Fatigue tests at room temperature is performed to build up an extensive and well-documented database. The testing specimen is a maltese cross thinned in its centre with non homogeneous strain/stress fields. The experimental protocol uses exclusively full-field strain measurements. The strains (cyclic and residual) as well as the crack initiation detection are obta...
متن کاملEffect of bonding temperature on the microstructure and electrochemical corrosion behavior of TLP bonded AISI 304L stainless steel
Transient liquid phase (TLP) bonding of AISI 304L stainless steel was carried out using BNi-2 amorphous interlayer. The microstructure of the joint area was studied by using optical and scanning electron microscopes and energy dispersive spectroscopy. The effect of bonding temperature (1030-1110 °C) was studied on the microstructure and corrosion behavior of the TLP bonded samples. Electrochemi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2011