Preparation of Pectin–ZnO Nanocomposite
نویسندگان
چکیده
Pectin-ZnO nanocomposite was prepared in the aqueous solution condition at room temperature. The Fourier transform infrared, X-ray diffraction, and transmission electron microscope (TEM) measurements confirmed the nanoscaled structure of pectin-ZnO composite. According to the TEM observation, the average composite granules size was about 150 nm and the embedded ZnO nanoparticles were uniform with an average diameter of 70 nm.
منابع مشابه
NANO EXPRESS Preparation of Pectin–ZnO Nanocomposite
Pectin–ZnO nanocomposite was prepared in the aqueous solution condition at room temperature. The Fourier transform infrared, X-ray diffraction, and transmission electron microscope (TEM) measurements confirmed the nanoscaled structure of pectin–ZnO composite. According to the TEM observation, the average composite granules size was about 150 nm and the embedded ZnO nanoparticles were uniform wi...
متن کاملPreparation of Polyaniline-Polystyrene-ZnO Nanocomposite and Characterization of Its Anti-Corrosive Performance
In this research, firstly polyaniline-zinc oxide (PANI-ZnO) nanocomposite was successfully synthesized by chemical polymerization of aniline in the presence of ZnO nanoparticles and then, 5%, 10% and 15% solutions of PANI–ZnO nanocomposites were mixed with a solution of polystyrene (PS) in tetrahydrofurane (THF) and PANI-PS-ZnO nanocomposites were obtained. The prepared nanocomposites were used...
متن کاملPreparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route
Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...
متن کاملPreparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route
Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...
متن کاملSynthesis and Characterization of Graphene-ZnO Nanocomposite and its Application in Photovoltaic Cells
In this paper, we present a simple method for preparation of graphene-ZnO nanocomposites (G-ZnO). The method is based on thermal treatment of the graphene oxide (GO)/ZnO paste which reduces the graphene oxide into the graphene and leads to the formation of the G-ZnO nanocomposite. The structure, morphology and optical properties of synthesized nanocomposites are characterized with XRD, FESEM, F...
متن کامل