Sub-100-nm silicon nanohole arrays were fabricated by a combination of the site-selective electroless deposition of noble metals through anodic porous alumina and the subsequent metal-assisted chemical etching. Under optimum conditions, the formation of deep straight holes with an ordered periodicity (e.g., 100 nm interval, 40 nm diameter, and high aspect ratio of 50) was successfully achieved. By using the present method, the fabrication of silicon nanohole arrays with 60-nm periodicity was also achieved.
منابع مشابه
Fabrication and Optical Characterization of Silicon Nanostructure Arrays by Laser Interference Lithography and Metal-Assisted Chemical Etching
In this paper metal-assisted chemical etching has been applied to pattern porous silicon regions and silicon nanohole arrays in submicron period simply by using positive photoresist as a mask layer. In order to define silicon nanostructures, Metal-assisted chemical etching (MaCE) was carried out with silver catalyst. Provided solution (or materiel) in combination with laser interference lithogr...
متن کاملInvestigation of HF/H2O2 Concentration Effect on Structural and Antireflection Properties of Porous Silicon Prepared by Metal-Assisted Chemical Etching Process for Photovoltaic Applications
Porous silicon was successfully prepared using metal-assisted chemical etching method. The Effect of HF/H2O2 concentration in etching solution as an affecting parameter on the prepared porosity type and size was investigated. Field emission electron microscopy (FE-SEM) confirmed that all etched samples had porous structure and the sample which was immersed into HF/H2O2 withmolar ratio of 7/3.53...
متن کاملSub-100 nm silicon nanowires by laser interference lithography and metal-assisted etching.
By combining laser interference lithography and metal-assisted etching we were able to produce arrays of silicon nanowires with uniform diameters as small as 65 nm and densities exceeding 2 x 10(7) mm(-2). The wires are single crystalline, vertically aligned, arranged in a square pattern and obey strict periodicity over several cm(2). The applied technique allows for a tailoring of nanowire siz...
متن کاملAu-Capped GaAs Nanopillar Arrays Fabricated by Metal-Assisted Chemical Etching
GaAs nanopillar arrays were successfully fabricated by metal-assisted chemical etching using Au nanodot arrays. The nanodot arrays were formed on substrates by vacuum deposition through a porous alumina mask with an ordered array of openings. By using an etchant with a high acid concentration and low oxidant concentration at a relatively low temperature, the area surrounding the Au/GaAs interfa...
متن کاملCatalyst Self-Assembly for Scalable Patterning of Sub 10 nm Ultrahigh Aspect Ratio Nanopores in Silicon.
Nanoporous silicon (NPSi) has received significant attention for its potential to contribute to a large number of applications, but has not yet been extensively implemented because of the inability of current state-of-the-art nanofabrication techniques to achieve sufficiently small pore size, high aspect ratio, and process scalability. In this work we describe the fabrication of NPSi via a modi...
متن کامل