Microstructural Characteristics of Geopolymers Based on Alkali-Activated Fly Ash
نویسنده
چکیده
Aluminosilicate geopolymers with a high silica molar ratio have been prepared by mixing Croatian coal-ash (ASTM Class F) and sodium silicate solution (water glass, technical grade). The samples were cured at 85 °C for 8 h and 24 h in different experimental conditions. Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM/EDS) have been used to identify the new phases formed in geopolymeric binders, and to follow the progress of their formation. It was observed that the glassy component of fly ash used reacted with water glass. The main reaction product formed in the geopolymeric materials was amorphous alkali aluminosilicate gel that induces a shift in the T–O (T=Si or Al) asymmetric stretching band towards lower frequency (1074.58 cm–1) in relation to the ones in the original fly ash. SEM/EDS detected a highly inhomogeneous glass-like matrix, constituted mainly of Na-Si-Al phases in a bulk region, together with unreacted spheres of fly ash particles.
منابع مشابه
Superplasticizer Addition to Carbon Fly Ash Geopolymers Activated at Room Temperature
Present concerns about global warming due to the greenhouse emissions in the atmosphere have pushed the cement industry to research alternatives to ordinary Portland cement (OPC). Geopolymer binder may constitute a possible breakthrough in the development of sustainable materials: understanding the effectiveness and the influences of superplasticizers on geopolymer systems is one of the essenti...
متن کاملMicrostructural and Mechanical Properties of Alkali Activated Colombian Raw Materials
Microstructural and mechanical properties of alkali activated binders based on blends of Colombian granulated blast furnace slag (GBFS) and fly ash (FA) were investigated. The synthesis of alkali activated binders was conducted at 85 °C for 24 h with different slag/fly ash ratios (100:0, 80:20, 60:40, 40:60, 20:80, and 0:100). Mineralogical and microstructural characterization was carried out b...
متن کاملEffect of Fly Ash Fineness on Sorption Properties of Geopolymers Based On Liquid Glass
Abstract—Fly ash (FA) thanks to the significant presence of SiO2 and Al2O3 as the main components is a potential raw material for geopolymers production. Mechanical activation is a method for improving FA reactivity and also the porosity of final mixture; those parameters can be analysed through sorption properties. They have direct impact on the durability of fly ash based geopolymer mortars. ...
متن کاملOne-part geopolymer mixes from geothermal silica and sodium aluminate
At present, the most commonly used building material is ordinary Portland cement (OPC). However, OPC has a negative environmental effect during synthesis, with the release of significant amount of CO2 greenhouse gas. The cement industry is responsible for 5-8% of total global anthropogenic CO2 emissions. Geopolymerization is a technology capable of turning industrial wastes into strong and chem...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2012