Crack Linkup by Stable Crack Growth
نویسندگان
چکیده
Experimentally determined T ε and CTOA resistance curves were used to simulate numerically, stable crack growth and the ensuing crack linkup in 0.8 mm thick 2024-T3 aluminum tension specimen with multiple site damage (MSD) subjected to monotonically/cyclically increasing loading. The T ε integral correctly predicted the crack growth and linkup history as well as the onset of rapid fracture in MSD specimens. The CTOA criterion also predicted the crack growth history but in its present form, could not predict crack linkup and rapid fracture. keyword: stable crack growth, crack linkup, T ε integral, CTOA, multiple site damage (MSD)
منابع مشابه
A Cohesive Zone Model for Crack Growth Simulation in AISI 304 Steel
Stable ductile crack growth in 3 mm thick AISI 304 stainless steel specimens has been investigated experimentally and numerically. Multi-linear Isotropic Hardening method coupled with the Von-Mises yield criterion was adopted for modeling elasto-plastic behavior of the material. Mode-I CT fracture specimens have been tested to generate experimental load-displacement-crack growth data during sta...
متن کاملThe Dc Electrical Potential Method for the Measumment of Fretting Cracks
As fretting fatigue cracks are initiated at an early stage of life, the fretting fracture process is dominated by the stable growth of cracks. Hence the measurement of crack length is very important. This paper demonstrates the suitability of the DC potential drop technique for the measurement of fretting cracks. A calibration has been established for monitoring crack growth in BS L65 copper al...
متن کاملCrack Tunneling: Effect of Stress Constraint
* Corresponding author; Email: [email protected] ABSTRACT Crack tunneling is a crack growth feature often seen in stable tearing crack growth tests on specimens made of ductile materials and containing through-thickness cracks with initially straight crack fronts. As a specimen is loaded monotonically, the mid-section of the crack front will advance first, which will be followed by crack growth ...
متن کاملNumerical Investigation on Stable Crack Growth in Plane Stress
Large deformation finite element analysis has been carried out to investigate the stress-strain fields ahead of a growing crack for compact tension (a/W=0.5) and three-point bend (a/W=0.1 and 0.5) specimens under plane stress condition. The crack growth is controlled by the experimental J-integral resistance curves measured by Sun et al. The results indicate that the distributions of opening st...
متن کاملResidual Strength Analyses of Riveted Lap-Splice Joints
Aging aircraft may develop multiple-site damage (MSD) that can reduce the structural integrity of fuselage structures. The existence of small cracks emanating from adjacent rivet holes in a fuselage lap-splice joint is of major concern. Small collinear cracks greatly reduce the residual strength of a panel with a lead crack. Recent studies predicting the residual strength of flat and curvilinea...
متن کامل