Investigation of Scaling Properties of Hysteresis in Finemet Thin Films
نویسنده
چکیده
We study the behavior of hysteresis loops in Finemet Fe73.5Cu1Nb3Si18.5B4 thin films by using a fluxometric setup based on a couple of well compensated pickup coils. The presence of scaling laws of the hysteresis area is investigated as a function of the amplitude and frequency of the applied field, considering sample thickness from about 20 nm to 5 μm. We do not observed any scaling predicted by theoretical models, while dynamic loops show a logarithmic dependence on the frequency.
منابع مشابه
Effect of Heat Treatment Time on the Characteristics of Coating Formed on Nanocrystalline Finemet Foils
In the present research, amorphous Fe73.5Si13.5B9Nb3Cu1 Finemet foils, 21-26µm in thickness and 5mm in width, were prepared by Planar Flow Casting (PFC) process. Wound cores of amorphous Finemet foils were simultaneously annealed and heat treated at 540°C for 60, 120 and 240 minutes in steam and air flow to form oxide insulating coating layer on both surfaces of the foils. The structure of nano...
متن کاملInvestigation of the mechanical properties of various yttria stabilized zirconia based thin films prepared by aqueous tape casting
In this study various yttria doped zirconia based thin films were prepared by the aqueous tape casting method. The rheological property of the paste was studies. The phase content and microstructure of the samples was investigated by X-ray diffraction and scanning electron microscope, respectively. The mechanical properties of thin films were studied by Vickers microhardness and nanoindentatio...
متن کاملFabrication of MgF2-SiO2 Nanocomposite Thin Films and Investigation of Their Optical and Hydrophobic Properties
In this research, MgF2-2%SiO2/MgF2 thin films were applied on a glass substrate. At first, MgF2 thin films with the optical thickness were deposited on the glass slide substrates. Then, MgF2-2%SiO2 thin films were deposited on the glass coated with MgF2 thin films. Finally, the nanocomposite thin films were surface treated by the PFTS solution. Characterization of the thin film was done by X-Ra...
متن کاملInvestigation of Structural, Morphological and Optical Properties of Chromium Oxide Thin Films Prepared at Different Annealing Times
Chromium oxide (α-Cr2O3) thin films were prepared using thermal annealing of chromium (Cr)films deposited on quartz substrates by direct current (DC) magnetron sputtering. The annealingprocess of the films was performed for different times of 60, 120,180 and 240 min. The influenceof annealing time on structural, morphological and optical properties of the prepared films wasinvestigated by diffe...
متن کاملDesign and investigation of TiO2 –SiO2 thin films on AISI 316L stainless steel for tribological properties and corrosion protection
The TiO2–SiO2 thin films were deposited on AISI 316L stainless steel via sol-gel method. Then, the effect of the added amount of SiO2 on the structure, morphology and mechanical properties of the films and corrosion behavior of AISI 316L stainless steel substrate were investigated. So, X-ray diffraction, field-emission scanning electron microscopy, atomic force microscopy, depth-sensing indenta...