Phase separation , thermal history and magnetic behaviour of Sr doped

High-resolution transmission electron microscopy observations and magnetic ac susceptibility measurements have been carried out to study the changes in the magnetic properties of La1−xSrxCoO3 samples (x 0.3) processed at different annealing temperatures, ranging from 1273 to 1573 K. Although neutron diffraction excludes the coexistence of distinct phases with different chemical composition, room temperature micrographs taken along the [0,−1, 1] rhombohedral zone-axis show bright fringes of different widths, extending over regions with sizes ranging from 8 to 40 nm. These regions are detected in all the samples, whatever the Sr content or the annealing temperature Ta . However, their number depends strongly on the processing conditions and becomes smaller and smaller as Ta increases. The periodicity of the bright fringes cannot be accounted for, either by variations in the sample thickness or by crystallographic defects, but it can be simulated if the presence of aperiodically alternate Sr-rich and La-rich (0, 1, 1) planes is assumed. On the other hand, the susceptibility measurements show that the amount of ferromagnetic phase present in each specimen depends on its thermal history. This suggests that the segregation of a second electronic phase takes place, the nucleation of which is influenced by the spatial homogeneity of the dopant distribution.