Bio-tribological properties and cytocompatibility of Ti-Si-N coatings
نویسندگان
چکیده
TieSieN coatings are synthesized on titanium alloy (Ti6Al4V) by arc-enhanced magnetron sputtering and the microstructure and tribological properties are determined. The friction coefficient of the TieSieN coatings, which is smaller in human serum than ambient air, decreases gradually with Si contents. Protein gel electrophoresis shows that the small friction coefficient is due to adsorbed proteins from the human serum under sliding conditions. The cytocompatibility of the coatings is assessed in vitro by a relative nitrite assay. The TieSieN coatings have a positive effect on nitric oxide synthesis on the endothelial cells. The cell morphology and spreading on the coatings are examined by fluorescence staining. The TieSieN coating with 12 at% Si exhibits the best effects in promoting actin cytoskeleton formation and cell spreading compared to coatings with different Si contents and titanium alloy. © 2015 Elsevier Ltd. All rights reserved.
منابع مشابه
Structural characteristics and tribological properties of TiAlCr(Si)CN nanocomposite films coated on the SPK 1.2080 tool steel using PVD technique
In the present work, structural characteristics and tribological properties of the Ti-Al-Cr-(Si)-C-N nanocomposite films coated on the SPK 1.2080 tool steel byPVD technique have been investigated. The PVD coating process was carried out using Ti (Si) Al and CrAl cathodes at 150 A current, 40 V bias and (Ar)0.1(CH4)0.45(N2)0.45 gas mixture for 50 min. Evaluations were conducted by OM, FESEM, AFM...
متن کاملEffect of Substrate Bias Voltage and Ti Doping on the Tribological Properties of DC Magnetron Sputtered MoSx Coatings
Molybdenum disulfide (MoS2) is one of the most widely used solid lubricants. In this work, composite MoSx/Ti coatings were deposited by direct-current magnetron sputter ion plating onto plain carbon steel substrates. The MoSx/Ti ratio in the coatings was controlled by sputtering the composite targets. The composition, microstructure, and mechanical properties of the coatings were explored using...
متن کاملEvaluation of tribological properties of (Ti,Al)CN/DLC composite coatings deposited by cathodic arc method.
In this study, Ti, Al and N doped DLC – referred to here after as “(Ti,Al)CN/DLC composite”- coating and pure diamond-like coating (DLC) were produced by cathodic arc deposition technique and the effects of the coating thickness on their tribological properties were evaluated. The coatings were characterized, using scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray diffrac...
متن کاملAnti-sticking behavior of DLC-coated silicon micro-molds
Pure carbon(C), nitrogen(N) and titanium(Ti) doped diamond-like carbon (DLC) coatings were deposited on silicon (Si) micro-molds by dc magnetron sputtering deposition to improve the tribological performance of the micro-molds. The coated and uncoated Si molds were used in injection molding for the fabrication of secondary metal-molds, which were used for the replication of micro-fluidic devices...
متن کاملSurface Characterization and Tribological Behaviour of Ti-Ni-P Intermetallic Coatings on Titanium Alloys
In this research, tribological behavior of Ti-Ni-P intermetallic coatings on titanium substrates have been investigated under dry reciprocating conditions. Hardness profile testing results exhibit that high surface hardness has been attained and static indentation result shows that the intermetallic coating has better adhesion strength than the conventional ceramic coatings. In this respect, th...
متن کامل