Microstructure of the highly dense MgB2 superconductor by transmission electron microscope
نویسندگان
چکیده
The microstructure of the MgB2 superconductor sintered at high temperature under a high pressure of ∼ 3 GPa was investigated by using a highresolution transmission electron microscope (HRTEM). The TEM images did not show any pores in the specimen. All grains were compactly connected, and no discernable empty spaces or impurities at the boundaries existed over the regions investigated. The HRTEM image showed clearly each constituent atom that formed the basal hexagonal plane, without any defect in a single grain. The a-axis lattice parameter, 0.307 nm, from this direct measurement ∗Correspondence should be addressed to Gun Yong Sung (e-mail: [email protected] )
منابع مشابه
Microstructure of the highly dense MgB2 Superconductor by TEM
The microstructure of the MgB2 superconductor sintered at high temperature under a high pressure of ∼ 3 GPa was investigated by using a highresolution transmission electron microscope (HRTEM). The TEM images did not show any pores in the specimen. All grains were compactly connected, and no discernable empty spaces or impurities at the boundaries existed over the regions investigated. The HRTEM...
متن کاملImproved Superconducting Properties in Bulk MgB2 Prepared by High Energy Milling of Mg and B Powder
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction (XRD), energy dispersive spectrometry (EDX) and scanning electron microscope (SEM), and the magnetization properties were examined by a Superconducting quantum ...
متن کاملساخت و بررسی تأثیر نانوذرات Sb2O3 بر ابررسانای 2223 – Bi
In this paper Sb2O3 nanoparticles are synthesized by solution method. The effect of these nanoparticles on the Bi-2223 superconductor properties has been investigated. The critical temperature, critical current density and activation energy were measured by the standard four-probe method. Magnetic properties of the samples were measured by using the AC magnetic susceptibility. The microstructur...
متن کاملخواص مغناطیسی و ساختاری ابررسانای 2223- Bi آلاییده با کادمیوم
In this paper, Bi1.64-xPb0.36CdxSr2Ca2Cu3Oy (BPCSCCO) superconductor with x = 0.0, 0.02, 0.04 and 0.06 is made by the solid state reaction method. The magnetic susceptibility measurements were performed using AC susceptometer. The microstructure and morphology of the samples have been studied by X-ray diffraction, scanning electron microscope and energy dispersive X-ray. The results show that t...
متن کاملEffect of Pre-existing Nano Sized Precipitates on Microstructure and Mechanical Property of Al-0.2wt% Sc Highly Deformed by ARB Process
The effect of pre-existing nano sized precipitates on the mechanisms and rate of grain refinement has been investigated during the severe plastic deformation. A binary Al–0.2Sc alloy, containing coherent Al3Sc particles, of 3.62 nm in diameter has been deformed by accumulative roll bonding up to 10 cycles. The resulting deformed structures were quantitatively analyzed using electron backscatter...