A Study of the Influence of Slag Alkali Level on the Alkali-Silica Reactivity of Slag Concrete
نویسندگان
چکیده
Ground granulated blast furnace slag (ggbs), can reduce the alkali load in concrete, despite its relatively high alkali content. Most research has been devoted to the efficacy of slag with an alkali content of less than 1.0% and this is reflected in guidance documents. A comparative assessment was made of the effect, if any, of the alkali level of ggbs on potential alkali-silica reactivity. Expansion tests were performed on a matrix of concrete mixes using Irish normal Portland cement, two slags of differing alkali content, three aggregates and alkali loads of 5 and 6 kg Na2Oeq./m . A replacement level of 50% was used throughout. No significant difference in behaviour was apparent, irrespective of aggregate type or alkali load, indicating that the alkali level of the slag is not a contributory factor at the 50% replacement level.
منابع مشابه
EFFECTS OF SILICA MODULUS AND ALKALI CONCENTRATION ON ACTIVATION OF BLAST-FURNACE SLAG
Abstract: The use of alkali-activated cementitious materials especially over the past decades has significantly been increased. The goal of this research is to investigate the effects of silica modulus and alkali concentration on alkali-activation of blast-furnace slag. In this research, the most important physical characteristics of cementitious systems, i.e. the 28-day compressive strength...
متن کاملSELF-Cured Alkali Activated Slag Concrete Mixes- An Experimental Study
Alkali Activated Slag Concrete (AASC) mixes are manufactured by activating ground granulated blast furnace slag (GGBFS) using sodium hydroxide and sodium silicate solutions. The aim of the present experimental research was to investigate the effect of increasing the dosages of sodium oxide (Na2O, in the range of 4 to 8%) and the activator modulus (Ms) (i.e. the SiO2/Na2O ratio, in the range of ...
متن کاملEco-Friendly Hybrid Concrete using Pozzolanic Binder and Glass Fibers
Hybrid Concrete focused on the development of buildings, highways, and other structures of civil engineering. In the current study, various mix combinations have been prepared and tested with different percentages of super-plasticizer at different levels of water reduction for obtaining the optimum mix. Further, study on different properties of hybrid concrete and replacement of ordinary portla...
متن کاملInvestigation on the effect of slag and limestone powder addition in alkali activated metakaolin
Alkali activated material has recently attracted great attention as an environmentally friendly building material. Generally, it exhibits higher mechanical properties and better durability when compared with Portland cement based materials. In this article, mixed alkali activated systems consisting of N-A-S-H and C-A-S-H hydrated gels were produced, using metakaolin as a dominated starting mate...
متن کامل