Green synthesis of shape-defined anatase TiO2 nanocrystals wholly exposed with {001} and {100} facetsw
نویسندگان
چکیده
منابع مشابه
Green synthesis of shape-defined anatase TiO2 nanocrystals wholly exposed with {001} and {100} facets.
Anatase TiO(2) nanocuboids wholly exposed with high-energy {001} and {100} facets were successfully synthesized by a novel, environmentally benign synthetic strategy using acid-delaminated vermiculite (DVMT) and tetramethylammonium hydroxide as synergistic morphology-controlling reagents, where the DVMT layers act as effective hard template selectively stabilizing the {001} facets of TiO(2).
متن کاملFluoride free synthesis of anatase TiO2 nanocrystals with exposed active {001} facets.
A novel fluoride free protocol for highly truncated anatase TiO2 nanocrystals with exposed {001} facets by preferential adsorption of CO3(2-) ions is developed. Experimental observations were corroborated by first principle quantum chemical DFT calculations. The synthesized anatase TiO2 showed improved photocatalytic activity.
متن کاملThe synthesis of nitrogen/sulfur co-doped TiO2 nanocrystals with a high specific surface area and a high percentage of {001} facets and their enhanced visible-light photocatalytic performance
Nitrogen/sulfur co-doped anatase TiO2 nanocrystals with a high specific surface area and a high percentage of {001} facets were synthesized by a solvent-thermal process followed by the calcination with thiourea at an optimum heat treatment temperature. Under current experimental conditions, the optimum heat treatment temperature was found at 300°C, which successfully introduced nitrogen and sul...
متن کاملSynthesis of micro-sized titanium dioxide nanosheets wholly exposed with high-energy {001} and {100} facets.
A new synthetic strategy was developed to prepare large-sized well-defined anatase TiO(2) nanosheets wholly dominated with thermodynamically unfavorable high-reactive {001} and {100} facets, which has a percentage of 98.7% and 1.3%, respectively. The as-prepared anatase TiO(2) nanosheets show a well-faceted morphology and have a large size in length (ca. 4.14 μm). The formation mechanism of the...
متن کاملLow-temperature synthesis of high-ordered anatase TiO2 nanotube array films coated with exposed {001} nanofacets
High-ordered anatase TiO2 nanotube array films coated with exposed high-reactive {001} nanofacets were fabricated by a modified hydrothermal method using amorphous anodic TiO2 nanotube arrays (ATONAs) as starting materials. It was found that the reaction between gas phase HF and solid ATONAs played a key role in the transformation process from amorphous to anatase TiO2, and the TiO2 tubular str...