Characterization of bioglass ceramic after addition of fluorine in Na2O-CaO-SiO2 system
نویسندگان
چکیده
Bioactive glass formed on the base sample (Go) of 45S5 system with fluorine additives samples were prepared by melt quenching method. The glassy samples were subjected to DTA for determining temperatures at which phase transition occur. FTTR spectroscopy shed a light on the sorts of compounds, their structure as well as their functional groups. The crystalline nature of samples was confirmed by XRD. The calculation of crystal size Xc revealed that the addition of fluorine as a network modifier didn’t affects the phase formation when the phase Na2CaSi3O8 was formed which is similar to the phase developed within the base sample (Go) the addition of fluorine also caused a shift of the glass transition temperature (Tg ) C, softening temperature (Ts) C, and crystallization temperature (Tc) C to lower values.
منابع مشابه
Preparation and characterization of fluorapatite-bioactive glass S53P4 nanocomposite
This research has been done to study characteristic and biocompatible evaluation of a nano-biocompositeceramic with the bioglass (BG) as a first phase. In this regard, synthesis of S53P4 (53% SiO2, 4% P2O5,23% Na2O and 20% CaO) bioglass has been considered as the first phase and flourapatite (FA) consideredas the second phase. Afterwards, nanocomposite with the base of S53P4 b...
متن کاملStudies on preparation and characterizations of CaO-Na2O-SiO2-P2O5 bioglass ceramics substituted with Li2O, K2O, ZnO, MgO, and B2O3
-The bioactive glass 45S5 (Hench glass), having composition 45 SiO2 24.5 Na2O 24.5 CaO -6 P2O5 (wt %) were prepared with substituted Li2O, K2O, ZnO, MgO, and B2O3 by conventional melting process in an electric globar furnace at 1400±10 OC. The Controlled crystallization were carried out to convert the bioglasses to their corresponding bioglass ceramics. Nucleation and crystallization regimes we...
متن کاملEFFECT OF TiO2 ADDITION ON BONDING STRENGTH OF CaO-P2O5 Na2O-TiO2 BIOACTIVE GLASS CERAMIC COATING
The effect of titanium dioxide addition on bonding strength of CaO-P2O5 -Na 2O-TiO2glass-ceramic system was investigated as a coating on titanium substrate. Thus, different amounts of TiO2 (2, 3.5 and 5mol %) were added to the base glass batch composition. The prepared glaze slips were applied on the substrate by dip coating method, dried and then heat treated at various temperatures. After tha...
متن کاملبررسی سنتز شیشه زیستفعال در سیستم Na2O–CaO –P2O5 – SiO2 به روش سل- ژل با استفاده از پیش مادههای مختلف
In this research, sol-gel bioactive glass in SiO2 �-P2O5 ? CaO - Na2O system using common nitrate precursors was investigated. Some parameters like water/alcohol/TEOS ratio, type of catalyst (acid or alkali) and temperature of heat treatment were also studied. Various precursors such as acetates, carbonates and chlorides were utilized to introduce Ca and Na in glass composition. Characterizatio...
متن کاملBioglass Dissolution: a Comparison between Sbf Solution and Hydrolytic Etching
The evaluation of chemical dissolution phenomena of the glasses in general is important because it is related to the bioactivity. This paper aims a comparative study of the bioglass dissolution between in vitro bioactivity test in SBF (Simulated Body Fluid) solution and the chemical durability test, in glasses on SiO2-Na2O-CaO with 6wt% de P2O5 system. The glasses were obtained by melting at 15...
متن کامل