A Mechanochemical Approach to Porous Silicon Nanoparticles Fabrication
نویسندگان
چکیده
Porous silicon samples have been reduced in nanometric particles by a well known industrial mechanical process, the ball grinding in a planetary mill; the process has been extended to crystalline silicon for comparison purposes. The silicon nanoparticles have been studied by X-ray diffraction, infrared spectroscopy, gas porosimetry and transmission electron microscopy. We have estimated crystallites size from about 50 nm for silicon to 12 nm for porous silicon. The specific surface area of the powders analyzed ranges between 100 m²/g to 29 m²/g depending on the milling time, ranging from 1 to 20 h. Electron microscopy confirms the nanometric size of the particles and reveals a porous structure in the powders obtained by porous silicon samples which has been preserved by the fabrication conditions. Chemical functionalization during the milling process by a siloxane compound has also been demonstrated.
منابع مشابه
Fabrication of p-Type Nano-porous Silicon Prepared by Electrochemical Etching Technique in HF-Ethanol and HF-Ethanol-H2O Solutions
Nano-porous silicon were simply prepared from p-type single crystalline silicon wafer by electrochemical etching technique via exerting constant current density in two different HF-Ethanol and HF-Ethanol-H2O solutions. The mesoporous silicon layers were characterized by field emission scanning electron microscopy and scanning electron microscopy. The results demonstrate that the width of nano-p...
متن کاملTailored porous silicon microparticles: fabrication and properties.
The use of mesoporous silicon particles for drug delivery has been widely explored thanks to their biodegradability and biocompatibility. The ability to tailor the physicochemical properties of porous silicon at the micro- and nanoscale confers versatility to this material. A method for the fabrication of highly reproducible, monodisperse, mesoporous silicon particles with controlled physical c...
متن کاملFabrication of porous silicon by metal-assisted etching using highly ordered gold nanoparticle arrays
A simple method for the fabrication of porous silicon (Si) by metal-assisted etching was developed using gold nanoparticles as catalytic sites. The etching masks were prepared by spin-coating of colloidal gold nanoparticles onto Si. An appropriate functionalization of the gold nanoparticle surface prior to the deposition step enabled the formation of quasi-hexagonally ordered arrays by self-ass...
متن کاملFabrication and Optical Characterization of Silicon Nanostructure Arrays by Laser Interference Lithography and Metal-Assisted Chemical Etching
In this paper metal-assisted chemical etching has been applied to pattern porous silicon regions and silicon nanohole arrays in submicron period simply by using positive photoresist as a mask layer. In order to define silicon nanostructures, Metal-assisted chemical etching (MaCE) was carried out with silver catalyst. Provided solution (or materiel) in combination with laser interference lithogr...
متن کاملNanostructures formed by displacement of porous silicon with copper: from nanoparticles to porous membranes
The application of porous silicon as a template for the fabrication of nanosized copper objects is reported. Three different types of nanostructures were formed by displacement deposition of copper on porous silicon from hydrofluoric acid-based solutions of copper sulphate: (1) copper nanoparticles, (2) quasi-continuous copper films, and (3) free porous copper membranes. Managing the parameters...
متن کامل