The characteristics of wet air oxidation of phenol over CuOx/Al2O3 catalysts: effect of copper loading.
نویسندگان
چکیده
The nature of active copper species is well-known to vary with copper loading, i.e., isolated Cu(2+) to bulk CuO. In this work, however, the effect of copper loading on the activity and the selectivity was investigated for the wet oxidation of phenol over CuO(x)/Al(2)O(3) catalysts. The activity and the mineralization selectivity of the catalysts increased with copper loading up to 7wt% and remained almost the same at a higher loading. The optimum copper loading was about 7wt% for the wet oxidation of phenol over CuO(x)/Al(2)O(3) catalysts in this work. The nature of copper species with different loading was characterized with TPR, XRD, and XANES. The chemical states of copper in the CuO(x)/Al(2)O(3) catalysts were confirmed as varying with copper loading: isolated Cu(2+) ions for 1wt%; highly dispersed Cu(2+) cluster for 5wt% and 7wt%, and bulk CuO for 10-25wt%. The stability of the CuO(x)/Al(2)O(3) catalysts with different copper loading was also studied with respect to carbonaceous deposits and copper leaching.
منابع مشابه
Preparation and performance analysis of γ-Al2O3 supported Cu-Ru bimetallic catalysts for the selective Wet Air Oxidation of Aqueous Ammonia to Nitrogen.
Series of Copper Ruthenium (Cu-Ru) bimetallic catalysts supported on γ-Al2O3 with different metal loading are prepared and investigated for catalytic wet air oxidation of ammonia to nitrogen. The ammonia decomposition activity was studied at three different temperatures i.e. 150oC, 200oC, and 230 oC and it is found that catalytic activity increases with the increase in temperature along with th...
متن کاملInfluence of Operational Parameters and Kinetic Modelling of Catalytic Wet Air Oxidation of Phenol by Al/Zr Pillared Clay Catalyst
Single and mixed oxide Al/Zr-pillared clay (Al/Zr-PILC) catalysts were synthesized and tested for catalytic wet air oxidation (CWAO) of aqueous phenol solution under milder conditions, in a semi-batch reactor. The catalysts were synthesized from natural bentonite clay using ultrasonic treatment during the aging and intercalation steps and were characterized <...
متن کاملOptimization and Modeling of CuOx/OMWNT’s for Catalytic Reduction of Nitrogen Oxides by Response Surface Methodology
A series of copper oxide (CuOx) catalysts supported by oxidized multi-walled carbon nanotubes (OMWNT’s) were prepared by the wet impregnation method for the low temperature (200 °C) selective catalytic reduction of nitrogen oxides (NOx) using NH3 as a reductant agent in the presence of excess oxygen. These catalysts were characterized by FTIR, XRD, SEM-EDS, and H2-TPR meth...
متن کاملMethanobactin-Mediated Synthesis of Gold Nanoparticles Supported over Al2O3 toward an Efficient Catalyst for Glucose Oxidation
Methanobactin (Mb) is a copper-binding peptide that appears to function as an agent for copper sequestration and uptake in methanotrophs. Mb can also bind and reduce Au(III) to Au(0). In this paper, Au/Al2O3 catalysts prepared by a novel incipient wetness-Mb-mediated bioreduction method were used for glucose oxidation. The catalysts were characterized, and the analysis revealed that very small ...
متن کاملWet Air Oxidation and Catalytic Wet Air Oxidation for Refinery Spent Caustics Degradation
The work focuses on evaluating wet air oxidation and catalytic wet air oxidation technique to degrade refinery spent caustics (original COD is 250,781 mg/L) in a milder operation conditions (150-200 ̊C, 0.2-2.5MPa). The results show that: in non-catalyst WAO, the highest COD degradation conversion could reach about 75% when 200 ̊C, 2MPa oxygen and 300rpm were used. At every temperature, the react...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemosphere
دوره 68 2 شماره
صفحات -
تاریخ انتشار 2007