Fengyuan Lu, Tiankai Yao, Yaron Danon, Jianren Zhou, Rodney C. Ewing, and Jie Lian Department of Mechanical and Industrial Engineering, Louisiana State University, Baton Rouge, Louisiana 70803 Department of Mechanical, Aerospace, and Nuclear Engineering, Rensselaer Polytechnic Institute, Troy, New York 12180 Department of Geological & Environmental Sciences, Stanford University, Stanford, California 94305-2115
منابع مشابه
Grain growth kinetic of spark plasma sintered magnesia
In this research, the densification of magnesia nanopowder with a mean particle size of about 100 nm was investigated by spark plasma sintering undera pressures of 80 MPa and at temperature range from 1000 °C to 1400 °C and a heating rate of 50 °C/min for 20 minutes. The density of the samples slowly increased with increasing sintering temperatures to 1200 °C. Afterwards, with more increasing o...
متن کاملIN SITU FABRICATION OF Al 2024-Mg2Si COMPOSITE BY SPARK PLASMA SINTERING OF REACTIVE MECHANICALLY ALLOYED POWDER
In situ Al2024- Mg2Si composite was fabricated by spark plasma sintering (SPS) of reactive powder. Reactive powder was obtained from mechanical alloying (MA) of elemental powders. Clad layers of in situ composite were fabricated on Al substrates by spark plasma sintering (SPS). Structural evolution during MA process and after SPS was investigated by X-ray diffractometery (XRD). Scanning electro...
متن کاملStability of Nanocrystalline Spark Plasma Sintered 3Y-TZP
Spark plasma sintered 3Y-TZP has been investigated with respect to hydrothermal ageing and grinding. The sintering was performed between the temperatures of 1,100 and 1,600 °C for a soaking time of 5 minutes and the resulting materials were obtained with grain sizes between 65 to 800 nm and relative densities between 88.5 to 98.8%. Experiments on hydrothermal ageing in water vapour at 131 °C, 2...
متن کاملMicrostructure of spark plasma sintered TiB2 and TiB2–AlN ceramics
In this research study, the effects of aluminum nitride (AlN) additive on the densification behavior and microstructure development of titanium diboride (TiB2) based ceramic matrix composite were investigated. In this way, a monolithic TiB2 ceramic and a TiB2–5 wt% AlN ultrahigh temperature ceramic composite were fabricated by spark plasma sintering (SPS) proces...
متن کاملFabrication of Nanostructured Cu matrix Nanocomposites by High Energy Mechanical Milling and Spark Plasma Sintering
Spark plasma sintering (SPS) is a sintering process that is capable of sintering hard worked powders in short times. This technique was used to fabricate bulk Cu and Cu-SiC nanocomposites. Pure Cu and mixed powders of Cu including 4 vol% of SiC nanoparticles were mechanically alloyed for 25 h and sintered at 750˚C under vacuum condition by SPS method. Microstructures of the materials were chara...