Co-Dispersion Behavior of ZrB2–SiC–B4C–C Powders with Polyethyleneimine
نویسندگان
چکیده
The aqueous dispersion behavior of ZrB₂, SiC powders with B₄C and C as sintering aids was investigated. Well co-dispersed suspension can be obtained in acidic solutions in presence of polyethyleneimine (PEI). The adsorption of PEI on the powder surface was measured by thermal gravimetric (TG) analysis. Rheological measurements displayed the effect of dispersant on the flow behavior of as-prepared slurries. An optimum condition was obtained with 1 wt % PEI. The viscosity of 40 vol % ZrB₂-SiC-B₄C-C (ZSBC) suspension at 100 s-1 was as low as 0.74 Pa·s, which was suitable for aqueous processing.
منابع مشابه
Fabrication and inspection of C/Cf-ZrB2-ZrC-SiC and C/Cf-ZrB2-SiC composite parts resistant to ablation by pressureless sintering method
In this research, the aim is to achieve strong and ablation-resistant composite parts C / Cf-ZrB2-ZrC-SiC and C / Cf-ZrB2-SiC by non-pressure sintering method. C / Cf-ZrB2-SiC samples were prepared using synthesized ZrB2 and SiC powders between layers of resin-impregnated carbon fabric. After pressing with pressure 5 times at 1600 وC and heat treatment for 2 hours in a controlled atmosphere fur...
متن کاملبررسی تاثیر میزان SiC و B4C و دمای زینتر بدون فشار بر خواص مکانیکی و مقاومت به اکسیداسیون ایزوترم نانو کامپوزیت های B4C -SiC- ZrB2
ZrB2 از جمله سرامیک های دما بالا با دمای ذوب بسیار بالای °C 3040 می باشد که خواص منحصر به فردی دارد. از مشکلات عمده ZrB2 زینتر پذیری ضعیف آن است که در این تحقیق با افزودن SiC در ابعاد میکرون و نانومتر، به عنوان فاز ثانویه و B4C به عنوان افزودنی سعی در رفع این مشکل گردید. مطالعات منظمی بر روی زینتر بدون فشار نانوکامپوزیت SiC-ZrB2 صورت پذیرفت. ابتدا به بررسی تغییرات اندازه ذرات در نتیجه زمانهای ...
متن کاملبررسی تأثیر افزودن ذرات دی سلیسید مولیبدن، کاربید بور و کاربید سیلیسیم بر استحکام خمشی و رفتار تف‌جوشی بدون فشار کامپوزیت فوق دما بالای ZrB2-HfB2
In this study, ZrB2-HfB2 composite was produced by pressureless sintering method. MoSi2 B4C and SiC particles were used as reinforcement. ZrB2 powder was milled in planetary ball mill apparatus and then reinforcement particles were added to the milled powder. The composite powders were then CIPed and sintered at 2100oC and 2150oC. Scanning electron microscopy (SEM) with an energy dispersive X-r...
متن کاملEffect of Silicon Carbide and graphite additives on the pressureless Sintering mechanism and microstructural characteristics of Ultra-High Temperature ZrB2 Ceramics Composites
The effect of SiC content, additives, and process parameters on densification and microstructural properties of pressureless sintered ZrB2– (1–10 wt %) SiC particulate composites have been studied. The ZrB2–SiC composite powders mixed by Spex mixer with 1-2wt% C (added as graphite powder) and CMC have been cold-compacted and sintered in argon environment in the temperature range of 1800–2100ºC ...
متن کاملOxidation of ZrB2-SiC Composites at 1600 °C: Effect of Carbides, Borides, Silicides, and Chopped Carbon Fiber
The aim of this work is to optimize the oxidation resistance of ZrB2-SiC-based composites with different additives. Effect of nine factors including SiC, Cf, MoSi2, HfB2 and ZrC contents, milling time of Cf (M.t) and SPS parameters such as temperature, time and pressure on oxidation resistance in four levels was investigated. Taguchi design was applied to explore effective parameters for ...
متن کامل