The mechanical and thick section bending behavior of friction stir processed aluminum plate
نویسندگان
چکیده
Friction stir processing (FSP) 2519-T87 aluminum plate results in enhanced ductility, 25% strain at fracture. However, the yield strength in the FSP zone drops to 175 MPa from �400 MPa. Actively cooling the plate during FSP increases the yield strength to 185 MPa and decreases ductility to 20% strain at fracture. Thick bending of a plate of the alloy was demonstrated after the surface was subjected to FSP.
منابع مشابه
Fabrication of Al/Graphite/Al2O3 Surface Hybrid Nano Composite by Friction Stir Processing and Investigating The Wear and Microstructural Properties of The Composite
Friction stir processing was applied for fabricating an aluminum alloy based hybrid nano composite reinforced with nano sized Al2O3 and micro sized graphite particles. A mixture of Al2O3 and graphite particles was packed into a groove with 1 mm width and 4.5 mm depth, which had been cut in 5083 aluminum plate of 10 mm thick. Packed groove was subjected to friction stir processing in order to im...
متن کاملEffects of Friction Stir Process Parameters on Microstructure and Mechanical properties of Aluminum Powder Metallurgy Parts
The effects of friction stir processing (FSP) on the microstructure and mechanical properties of aluminum powder metallurgy (PM) parts was investigated. PM parts were then subjected to FSP at advancing speeds (v) of 40-200 mm/min and tool rotational speeds (ω) of 800-1600 rpm. Microhardness (HV) and tensile tests at room temperature were used to evaluate the mechanical properties of the frictio...
متن کاملEvaluation of fatigue behavior of cast and ultra-fine processed Al-7075 by using friction stir technique
This paper presents experimental results on the fatigue properties of the modified microstructure of cost Al-alloy 7075 via friction stir processing (FSP). The microstructural behavior was investigated by using optical microscope (OM). The grain size of cast FSP-ed at different locations was investigated via XRD. Uniaxial tensile and bending fatigue tests were carried out at room temperature o...
متن کاملEvaluation of fatigue behavior of cast and ultra-fine processed Al-7075 by using friction stir technique
This paper presents experimental results on the fatigue properties of the modified microstructure of cost Al-alloy 7075 via friction stir processing (FSP). The microstructural behavior was investigated by using optical microscope (OM). The grain size of cast FSP-ed at different locations was investigated via XRD. Uniaxial tensile and bending fatigue tests were carried out at room temperature o...
متن کاملA study on the sub-structure and mechanical properties of friction stir processed AA 6061-T6 joints with ultra-fine grained structure
Ultra-fine grained (UFG) structure (~0.6 µm) was produced in the stir zone (SZ) of 6061-T6 aluminum alloy joints using friction stir processing (FSP) cooled by liquid nitrogen (N2). A new experimental set-up was used to simultaneously quench the lower and upper surfaces of the samples during the processing. In addition, FSPed joints, using a steel backing plate, were produced at room temperatur...
متن کامل