Silicon nanoparticles synthesised through reactive high-energy ball milling: enhancement of optical properties from the removal of iron impurities
نویسندگان
چکیده
Alkyl-terminated silicon nanoparticles (SiNPs) were prepared through reactive high-energy ball milling with contamination of iron from the steel milling materials. Iron impurities in the form of iron nanoparticles cause a decrease of photoluminescence intensity and an increase of the UV absorption. The iron impurities were removed either by gel permeation chromatography separation or by treatment with an aqueous HCl solution. The photoluminescence properties of the SiNPs were enhanced after the removal of iron. Transmission electron microscopy, energy-dispersive X-ray spectroscopy, Fourier transform infrared spectroscopy and proton nuclear magnetic resonance were used to determine morphology, elemental composition and surface passivation of SiNPs.
منابع مشابه
Evaluation of catalyst ball-milling process on growth and diameter of carbon nanotubes on iron nanoparticles
In this study, we describe the growth of carbon nanotubes on commercial iron nanoparticles without carbon shell (Fe (nm), size 2O3 and Fe* (nm)/MgO) was carried out by mixing commercial Fe* nanoparticles (as catalyst) with Al2O3 and MgO powders (as supports)by using ball-milling method. The results show in spite of the fact that ball-milling process can have neg...
متن کاملEvaluation of catalyst ball-milling process on growth and diameter of carbon nanotubes on iron nanoparticles
In this study, we describe the growth of carbon nanotubes on commercial iron nanoparticles without carbon shell (Fe (nm), size 2O3 and Fe* (nm)/MgO) was carried out by mixing commercial Fe* nanoparticles (as catalyst) with Al2O3 and MgO powders (as supports)by using ball-milling method. The results show in spite of the fact that ball-milling process can have neg...
متن کاملبررسی تغییرات فازی سیلیس و سیلیسیوم به هنگام آسیاب کاری
In the present study phase transformation of silicon and silica during milling in different atmospheres was investigated. The silicon powder was subjected to high energy ball milling in ammonia (25%) atmosphere. The milled powder was subsequently annealed at 1200 ◦C for 1 hour. In another test a mixture of AlN and amorphous silica (micro silica) was subjected to high energy ball milling. The m...
متن کاملStrain dependence of the nonlinear optical properties of strained Si nanoparticles.
We report on the lattice strain dependence of the nonlinear optical (NLO) parameters of strained Si nanoparticles (NPs), which are prepared in a controlled way by a mechanical ball milling process. X-ray diffraction analysis shows that the nature of strain is compressive and is primarily caused by milling-induced lattice dislocations, which is further supported by high-resolution transmission e...
متن کاملEffect of CaO on the Formation of PSZ and γ-Zirconia Nanoparticles through Ball Milling
The effect of CaO on the formation of β- and γ-zirconia nanoparticles from α-zirconia was investigated and their stability evaluated via mechanical activation. α-ZrO2+8.5wt%CaO powder was milled for 2-150 hours with ball-to-powder weight ratios (BPWR) of 40:1 and 60:1. Structural evaluations were conducted using X-Ray diffraction and scanning electron microscope (SEM). Thermal analysis wa...
متن کامل