The wear of high-carbon metal-on-metal bearings after different heat treatments.
نویسندگان
چکیده
To study the tribological performance of metal-on-metal hip joint resurfacings, the wear performance of three pairs of Co-Cr-Mo alloy samples (pins and plates) were tested in a multidirectional pin-on-plate wear machine. An 'as-cast', a single-heat-treated, and a double-heat-treated set of specimens were tested to 3 x 10(6) cycles. The two heat treatments resulted in partial and full solution of the carbides into the matrix. An increasing trend in wear rate was found from 'as-cast' to the double-heat-treated specimens. The as-cast specimens showed the lowest wear rate (1.69 x 10(-6) mm3/N m), the reduced carbide samples had the next lowest wear rate (2.1 x 10(-6) mm3/N m), while the specimens without carbides wore the most (2.41 x 10(-6) mm3/N m).
منابع مشابه
Ten-year results of a double-heat-treated metal-on-metal hip resurfacing.
Second-generation metal-on-metal bearings were introduced as a response to the considerable incidence of wear-induced failures associated with conventional replacements, especially in young patients. We present the results at ten years of a consecutive series of patients treated using a metal-on-metal hip resurfacing. A distinct feature of the bearings used in our series was that they had been ...
متن کاملTribological performance of various CoCr microstructures in metal-on-metal bearings: the development of a more physiological protocol in vitro.
Hip simulators have been used for ten years to determine the tribological performance of large-head metal-on-metal devices using traditional test conditions. However, the hip simulator protocols were originally developed to test metal-on-polyethylene devices. We have used patient activity data to develop a more physiologically relevant test protocol for metal-on-metal devices. This includes sto...
متن کاملWear Performance of Ceramic-On-Metal Hip Bearings
Ceramic-on-metal (CoM) bearings are considered to be a promising alternative to polyethylene-based bearings or hard-on-hard bearings (Ceramic-on-Ceramic (CoC) and Metal-on-Metal (MoM)). Although, CoM shows lower wear rates than MoM, in-vitro wear testing of CoM shows widely varying results. This may be related to limitations of wear-measuring methods. Therefore, the aim of this study was to imp...
متن کاملEffect of carbon ion implantation on the tribology of metal-on-metal bearings for artificial joints
Metal-on-metal (MoM) bearings have become popular due to a major advantage over metal-on-polymer bearings for total hip arthroplasty in that the larger femoral head and hydrodynamic lubrication of the former reduce the rate of wear. However, concerns remain regarding adverse reactions to metal debris including metallosis caused by metal wear generated at the taper-head interface and another mod...
متن کاملGas tungsten arc welding of direct quenched wear resistant steel to plain carbon steel and evaluation of its microstructure and wear properties
In this research, the dissimilar welding of St52 plain carbon steel to W400 wear resistant steel and its effect on the microstructure and wear properties of the wear resistant steel was investigated. The wear resistant steel was produced via direct quenching with nominal hardness of 400 HB. Gas tungsten arc welding was used for joining process. The results showed that welding led to hardness re...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Proceedings of the Institution of Mechanical Engineers. Part H, Journal of engineering in medicine
دوره 222 6 شماره
صفحات -
تاریخ انتشار 2008