The Preparation and Characterization of Pyrolysis Bio-Oil-Resorcinol-Aldehyde Resin Cold-Set Adhesives for Wood Construction

نویسندگان

  • Xueyong Ren
  • Hongzhen Cai
  • Hongshuang Du
  • Jianmin Chang
  • Antonio Pizzi
چکیده

Resorcinol-formaldehyde (RF) resin is a kind of excellent exterior-grade wood structural adhesive, which can be conveniently cold-set for various applications. In order to decrease the production cost, pyrolysis bio-oil from renewable bioresources was used to replace resorcinol to synthesize the bio-oil-resorcinol-aldehyde (BRF) resin. The effect of replacing resorcinol with bio-oil on the properties, bonding performance, and characterization of resorcinol-aldehyde resin was comparatively investigated. A higher solid content and viscosity, albeit a lower shear strength, was found when the replacement ratio of bio-oil increased. The bonding performance of BRF with 10 and 20 wt % bio-oil was close to that of the pure RF resin. However, the trends of being less cross-linked, more easily decomposed, but more porous were found when the substitution ratio of bio-oil was higher than 20 wt %. Interestingly, it was found that the wood failure values of the BRF resins with bio-oil of no more than 20 wt % were slightly higher than that of the pure RF resin. On the whole, BRF resins with 20 wt % bio-oil is recommended as a wood structural adhesive, comprehensively considering the bio-oil substitution ratio and resin properties. The results obtained here showed that pyrolysis bio-oil is a promising green raw material for the production of RF resin with lower cost.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Preparation and Characterization of Epoxy Resin Cross-Linked with High Wood Pyrolysis Bio-Oil Substitution by Acetone Pretreatment

The use of cost effective solvents may be necessary to store wood pyrolysis bio-oil in order to stabilize and control its viscosity, but this part of the production system has not been explored. Conversely, any rise in viscosity during storage, that would occur without a solvent, will add variance to the production system and render it cost ineffective. The purpose of this study was to modify b...

متن کامل

Preparation and Characterization of a Phenol-formaldehyde Resin Adhesive Obtained From Bio-ethanol Production Residue

Phenol formaldehyde (PF) resins are widely used as wood adhesives in the industrial production of exterior-grade plywood panels, oriented strand board panels and particleboards due to their superior performance including high bonding strength, heat resistance, excellent water resistance and chemical stability1. However, phenol, one raw material for the synthesis of PF resins, is a petroleum-bas...

متن کامل

Wood Adhesion and Adhesives

9.1 General..................................................................................................................................216 9.2 Wood Adhesive Uses............................................................................................................217 9.3 Terminology..........................................................................................................

متن کامل

A Review of the Chemical and Physical Mechanisms of the Storage Stability of Fast Pyrolysis Bio-Oils

........................................................................................................................ 1 1.0 Introduction .......................................................................................................................... 1 1.1 Storage Stability Problem.......................................................................... 1 1.2 Combustion Problems Ca...

متن کامل

THEIR USE IN WOOD-LAMINAnNG ADHFSIVES: AN EXPLORATORY STUDY

The reaction of a tannin extract (containing about 30"/0 carbohydrate) from loblolly pine (Pinus taeda L.) bark (two parts) and resorcinol (one part) at 12O"C for 24 h with acetic acid catalyst gave a product containing predominantly oligomeric procyanidin-4-resorcinol adducts (3Wo), unreacted resorcinol (22%). carbohydrate (20010). the resorcinol adduct 2R,3R,4S 4-(2.4-dihydroxyphenyl).fIavan-...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2017