Fabrication of κ-Carrageenan Fibers by Wet Spinning: Spinning Parameters
نویسندگان
چکیده
This study demonstrates the fabrication of κ-carrageenan fibers by a wet-spinning method and discusses three important spinning parameters: coagulation bath composition, spinning rate and post-spinning mechanical drawing. The as-spun fiber diameter decreased with KCl and ethanol concentration in the coagulation bath. In general, the ultimate tensile stress and elongation at break both increased for KCl concentration from 0.1 to 0.5 M with and without ethanol, with no significant change above 0.5 M. Spinning rate affected the dope flow and thus the polymer orientation (apparent viscosity) and fiber morphology. At spinning rates between 0.25 mL/min and 0.33 mL/min, the fiber diameter reached a minimum and the fiber surface was smooth. Both an increase and decrease from this spinning rate range increased the fiber diameter and roughness of the fiber surface. Post-spinning drawing of the fiber resulted in even smaller fiber diameter.
منابع مشابه
Fabrication of Biodegradable PCL Particles as well as PA66 Nanofibers via Air-Sealed Centrifuge Electrospinning (ASCES)
This study presents a method for fabrication of ultrafine polymeric nanofibers as well as nano/micro particles utilizing centrifugal and electrostatic forces simultaneously. To reduce the diameter and variety of nanofibers produced from solid state polymerized PA66, a unique electrocentrifuge spinning device was utilized with a rotating nozzle and collector, while the fabrication process (spinn...
متن کاملVersatile Molding Process for Tough Cellulose Hydrogel Materials
Shape-persistent and tough cellulose hydrogels were fabricated by a stepwise solvent exchange from a homogeneous ionic liquid solution of cellulose exposure to methanol vapor. The cellulose hydrogels maintain their shapes under changing temperature, pH, and solvents. The micrometer-scale patterns on the mold were precisely transferred onto the surface of cellulose hydrogels. We also succeeded i...
متن کاملStudy on the Damaging of Dyed Cotton Fibers with Direct Dye in Spinning Processes and its Effect on the Properties of Cotton Mélange Yarn
The influence of dyeing and spinning on the characteristics of cotton fibers and its impact on the properties of cotton mélange yarn has been investigated. Grey cotton fibers with mean fiber length and fineness of 29 mm and 4.2 micronair were pre-treated and dyed. Three ring yarns were spun from 100 % grey cotton (R.R.Y), 50-50 % blend of dyed and grey cotton (M.R.Y) and 100 % dyed cotton fiber...
متن کاملThe Preparation and Characterization of Poly(m-phenyleneisophthalamide) Fibers Using Ionic Liquids
A process to produce fibers from Poly(m-phenyleneisophthalamide)(PMIA) solution in an ionic liquid via wet-spinning technology are described. The spinning process was investigated on a small laboratory scale. Ionic liquid spinning solutions were first prepared for PMIA fibers, followed by wet spinning. In the course of this research, the physical properties of the PMIA fibers were estimated. We...
متن کامل