Phage-directed synthesis of copper sulfide: structural and optical characterization.

The growth of crystalline copper sulfide using a viral template was investigated using sequential incubation in CuCl2 and Na2S precursors. Non-specific electrostatic attraction between a genetically-modified M13 bacteriophage and copper cations in the CuCl2 precursor caused phage agglomeration and bundle formation. Following the addition of Na2S, polydisperse nanocrystals 2-7 nm in size were found along the length of the viral scaffold. The structure of the copper sulfide material was identified as cubic anti-fluorite type Cu1.8S, space group Fm3[overline]m. Strong interband absorption was observed within the ultraviolet to visible range with an onset near 800 nm. Furthermore, free carrier absorption, associated with the localized surface plasmon resonance of the copper sulfide nanocrystals, was seen in the near infrared with absorbance maxima at 1060 nm and 3000 nm, respectively.