Rebonding performance of different ceramic brackets conditioned with a new silane coupling agent.
نویسندگان
چکیده
The objective of this study was to investigate the rebonding effect of a new silane coupling agent on various ceramic brackets bonded to ceramic specimen. Different ceramic brackets (Fascination 2, Clarity SL, and In-OvationC) were assigned to three groups: rebonding with new silane coupling agent, rebonding with conventional silane coupling agent, or regular bonding as control (n = 16). Bracket adhesion was calculated with a shear test in a universal testing machine. The bracket-composite-ceramic interface was evaluated using the adhesive remnant index score. One-way analysis of variance was applied for inferential statistics. Rebonding with the new silane coupling agent resulted in high shear bond strengths (SBSs; mean values: 37.44-41.24 MPa) and ceramic specimen fractures. Rebonding with the conventional silane coupling agent resulted in significantly (P < 0.001) lower clinically adequate SBS (mean values: 20.20-29.92 MPa) with the least ceramic specimen fractures. Regularly bonded ceramic brackets resulted in clinically adequate to high SBS (mean values: 17.06-41.56 MPa) depending on their bracket base design. Rebonded ceramic brackets showed sufficient SBS to ceramic specimen surfaces. However, increased bracket adhesion was associated with a risk of ceramic specimen surface damage. Therefore, ceramic brackets rebonded with the new silane coupling should be debonded cautiously using alternative debonding methods.
منابع مشابه
Porcelain surface-conditioning techniques and the shear bond strength of ceramic brackets.
The aim of this study was to compare the effects of various porcelain surface-conditioning techniques, used either alone or in combination, on the shear bond strength (SBS) of ceramic brackets cured with a light emitting diode (LED). Thirty glazed porcelain facets were randomly divided into three groups of 10. In group I, the porcelain surfaces were etched with 9.6 per cent hydrofluoric acid (H...
متن کاملSilane and bonding of Resins to Ceramic
Silane and bonding of Resins to Ceramic Dr. K. Seyyedan* - Dr. M. Kalalipoor** - Dr. M. Javan***Assistant Professor of Fixed Prosthodontics Dept., Faculty of Dentistry, Shaheed Beheshti University of Medical Sciences. **Resident of Fixed Prosthodontics Dept., Faculty of Dentistry, Shaheed Beheshti University of Medical Sciences. Background and Aim: When bonding between two different dental mate...
متن کاملAssessment of Bond Strength between Metal Brackets and Non-Glazed Ceramic in Different Surface Treatment Methods
OBJECTIVE The aim of this study was to evaluate the bond strength between metal brackets and non-glazed ceramic with three different surface treatment methods. MATERIALS AND METHODS Forty-two non-glazed ceramic disks were assigned into three groups. Group I and II specimens were etched with 9.5% hydrofluoric acid. Subsequently in group I, silane and adhesive were applied and in group II, bond...
متن کاملComparison of shear bond strength of metal brackets bonded to porcelain surface using different surface conditioning methods: an in vitro study.
AIM To evaluate and compare the shear bond strength of metal brackets bonded to ceramic surfaces using different conditioning methods and to assess the site of bond failure after debonding. MATERIALS AND METHODS A total of 70 ceramic surfaces were produced with uniform shape, size and composition. The samples were divided into 7 groups (each of 10 samples). Group 1 was the control group (untr...
متن کاملEffect of bonding material, etching time and silane on the bond strength of metallic orthodontic brackets to ceramic.
The purpose of this study was to evaluate the bond strength of metallic orthodontic brackets to feldspathic ceramic with different etching times, bonding materials and with or without silane application. Cylinders of feldspathic ceramic were etched with 10% hydrofluoric acid for 20 or 60 s. For each etching time, half of the cylinders received two layers of silane. Metallic brackets were bonded...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- European journal of orthodontics
دوره 35 1 شماره
صفحات -
تاریخ انتشار 2013