Oxygen reduction via grain boundary transport in thin film platinum electrodes on yttria stabilized zirconia
نویسندگان
چکیده
Model-type sputter deposited platinum microelectrodes with different grain sizes were investigated on single crystalline yttria stabilized zirconia (YSZ) by means of impedance spectroscopy. Measurements on single platinum microelectrodes could be continuously performed for > 100 h and from 250 to 800 °C without losing contact. From the temperature dependence, two parallel reaction pathways for oxygen reduction could be identified. Above 450 °C, a surface path with a rate determining step located at the three phase boundary is predominant. Its polarization resistance is independent of the Pt grain size and exhibits an activation energy of ca. 1.8 eV. In the low temperature regime (< 450 °C) a bulk path through Pt was verified, with an electrode polarization resistance depending on the Pt grain size. This resistance is only slightly thermally activated and the rate limiting step is most probably oxygen diffusion along Pt grain boundaries.
منابع مشابه
Characterization of the Electrochemical Performance of YSZ Thin
In this work, thin film yttria-stabilized zirconia [YSZ] solid electrolytes were sputtered onto insulating substrates at room temperature and 600oC in order to produce different average grain sizes (~15-50 nm). For reference, polished samples of single crystal and bulk, poly-crystalline YSZ were also used. Platinum film electrodes were then sputtered on top and lithographically patterned to giv...
متن کاملThe Vapor Deposition and Oxidation of Platinum- and Yttria-Stabilized Zirconia Multilayers
Attempts to increase the gas temperature within gas turbine engines are driving the development of thermal barrier coatings that reduce superalloy component oxidation rates by disrupting thermal transport processes. Novel metal–ceramic multilayer’s combining thin metal layers with low thermal conductivity oxide ceramics offer a potential approach for impeding both the radiative and conductive t...
متن کاملPlatinum-Based Nanowire Networks with Enhanced Oxygen-Reduction Activity
Pt-Al and Pt-Y-Al thin-film electrodes on yttria-stabilized zirconia electrolytes were prepared by dealloying of cosputtered Pt-Al or Pt-Y-Al films. The selective dissolution of Al from the Pt-alloy compound causes the formation of a highly porous nanowire network with a mean branch thickness below 25 nm and a pore intercept length below 35 nm. The oxygen-reduction capability of the resulting e...
متن کاملEffect of ion implantation doping on electrical properties of yttria-stabilized zirconia thin films
The change in conductivity of Fe and Ti implanted if-sputtered layers of yttria-stabilized zirconia (YSZ) was studied as a function of the temperature (400-800 °C) and oxygen partial pressure. In an oxidized state and in the temperature range of 400600 ° C, the conductivity of the Fe implanted YSZ film ( 15 keV, 8 × 10 '6 at.cm 2) was dominated by the n-type electronic conductivity of a thin Fe...
متن کاملA New Low-Temperature Electrochemical Hydrocarbon and NOx Sensor
In this article, a new investigation on a low-temperature electrochemical hydrocarbon and NOx sensor is presented. Based on the mixed-potential-based sensing scheme, the sensor is constructed using platinum and metal oxide electrodes, along with an Yttria-Stabilized Zirconia (YSZ)/Strontium Titanate (SrTiO₃) thin-film electrolyte. Unlike traditional mixed-potential sensors which operate at high...