The effects of phosphoric acid and pyrolysis temperature to the formation of flaky graphite from lignite
نویسنده
چکیده
The flaky graphites were prepared from lignite. The effects of phosphoric acid ratios and pyrolysis temperatures on flake formation were studied by SEM, TEM and XRD. The results showed that the flaky graphite occurred at a pyrolysis temperature of 600°C with a 1.0:1.0 ratio of carbon to phosphoric acid. The flaky formation was almost completed by pyrolysis at 800°C and with a 1:2.0 ratio of carbon to phosphoric acid. The flaky graphite had a thickness and lateral dimension of about 50 nm and 2 μm.
منابع مشابه
Effects of Modified Pyrolysis Tar on Gas Desulphurization Performance
The paper introducedeffects of modified pyrolysis tar on flue gas desulfurization. This experiment selected the pyrolysis tar as the raw material, researched the effects on desulfurization performance under different modification solution, concentration, solid liquid ratio of pyrolysis tar and modified solution, calcination temperature and calcination time by 16 group orth...
متن کاملElectrocatalytic oxidation of ethanol on the surface of the POAP/ phosphoric acid-doped ionic liquid-functionalized graphene oxide nanocomposite film
In situ electropolymerization as a facile synthetic procedure has been used to obtain highly active compositesof ionic liquid functionalized graphene oxide(FGO)and poly ortho aminophenol (POAP). Surface and electrochemical analysis have been used for characterisation of FGO-POAP composite film. Nickel was accumulated by complex formation between Ni (II) in solution and amines sites in the polym...
متن کاملElectrocatalytic oxidation of ethanol on the surface of the POAP/ phosphoric acid-doped ionic liquid-functionalized graphene oxide nanocomposite film
In situ electropolymerization as a facile synthetic procedure has been used to obtain highly active compositesof ionic liquid functionalized graphene oxide(FGO)and poly ortho aminophenol (POAP). Surface and electrochemical analysis have been used for characterisation of FGO-POAP composite film. Nickel was accumulated by complex formation between Ni (II) in solution and amines sites in the polym...
متن کاملPretreatment of Gray Cast Iron for Hard Chromium Electroplating (RESEARCH NOTES)
From the standpoint of processing, hard chromium layer plate may be applied to steels, cast iron, aluminum and nickel base alloys. Cast iron can be plated provided that the surface is capable of conducting the required current and is reasonably free of voids, pits, gross silicate inclusions, and massive segregation. There are many difficulties arising from graphite phase and deposition of hydro...
متن کاملSurfactant-Aided Phosphoric Acid Pretreatment to Enable Efficient Bioethanol Production from Glycyrrhiza Glabra Residue
Glycyrrhiza glabra residue (GGR) was efficiently subjected to concentrated phosphoric acid (PA) pretreatment with/without surfactant assistance, and promising results were obtained following separate enzymatic hydrolysis and fermentation (SHF) of the biomass. Pretreatment was carried out using 85 % PA either at 50 or 85 °C with 12.5 % solid loading for 30 min. In parallel experiments, ...
متن کامل