Effects of Stirrups on Bond Behavior Between Concrete and Corroded Steel Bars
نویسندگان
چکیده
Steel corrosion leads to the deterioration of bond between concrete and steel bars. The serviceability and ultimate strength of concrete elements within RC structures are hence affected. Many researchers have studied the bond behavior of corroded steel bars. However, very few studies have investigated the effects of confinements on the degradation of bond strength. The present paper proposed a new kind of beam specimen based on which the effects of stirrups on degradation of bond were investigated. The test results proved that stirrups can effectively increase the bond strength between concrete and corroded steel bars.
منابع مشابه
An Experimental Study on Effect of Steel Corrosion on the Bond–Slip Performance of Reinforced Concrete
This paper studied the effects of reinforcement corrosion on bond performance between rebar and concrete. Tests were carried out to evaluate the degradation of bond between reinforcing steel and concrete for different corrosion levels of reinforcing steel. A series of 20 specimens of different concrete strength with various reinforcing steel corrosion levels were designed and manufactured. Each...
متن کاملReliability Analysis of Corroded Reinforced Concrete Beams Using Enhanced HL-RF Method
Steel corrosion of bars in concrete structures is a complex process which leads to the reduction of the cross-section bars and decreasing the resistance of the concrete and steel materials. In this study, reliability analysis of a reinforced concrete beam with corrosion defects under the distributed load was investigated using the enhanced Hasofer-Lind and Rackwitz-Fiessler (EHL-RF) method base...
متن کاملModelling the loss of steel-concrete bonds in corroded reinforced concrete beams
The existing stochastic models for deterioration of reinforced concrete structures is extended by adding modelling of “loss of bond” due to corrosion between the reinforcement bars and the surrounding concrete.
متن کاملPrediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures
This paper presents an experimental investigation on the crack width induced by the corrosion of reinforcing steel bars in concrete. Reinforcing steel bars with different diameters were corroded using an accelerated test in three types of concrete members, including 24 beams with corroded stirrup and 20 beams with corroded longitudinal reinforcing steel bars. The corrosion patterns and rusts ch...
متن کاملCorrosion Assessment of Steel Bars Used in Reinforced Concrete Structures by Means of Eddy Current Testing
This paper presents a theoretical and experimental study on the use of Eddy Current Testing (ECT) to evaluate corrosion processes in steel bars used in reinforced concrete structures. The paper presents the mathematical basis of the ECT sensor built by the authors; followed by a finite element analysis. The results obtained in the simulations are compared with those obtained in experimental tes...
متن کامل