The Mechanism of Pseudomorphic Transformation of Spherical Silica Gel into MCM-41 Studied by PFG NMR Diffusometry

نویسندگان

  • Wolf-Dietrich Einicke
  • Dirk Enke
  • Muslim Dvoyashkin
  • Rustem Valiullin
  • Roger Gläser
چکیده

The pseudomorphic transformation of spherical silica gel (LiChrospher® Si 60) into MCM-41 was achieved by treatment at 383 K for 24 h with an aqueous solution of cetyltrimethylammonium hydroxide (CTAOH) instead of hexadecyltrimethylammonium bromide (CTABr) and NaOH. The degree of transformation was varied via the ratio of CTAOH solution to initial silica gel rather than synthesis duration. The transformed samples were characterized by N₂ sorption at 77 K, mercury intrusion porosimetry, X-ray diffraction (XRD) and scanning electron microscopy (SEM). Thus, MCM-41 spheres with diameters of ca. 12 μm, surface areas >1000 m² g-1, pore volumes >1 cm³ g-¹ and a sharp pore width distribution, adjustable between 3.2 and 4.5 nm, were obtained. A thorough pulsed field gradient nuclear magnetic resonance (PFG NMR) study shows that the diffusivity of n-heptane confined in the pores of the solids passes through a minimum with progressing transformation. The final product of pseudomorphic transformation to MCM-41 does not exhibit improved transport properties compared to the initial silica gel. Moreover, the PFG NMR results support that the transformation occurs via formation and subsequent growth of domains of <1 μm containing MCM-41 homogeneously distributed over the volume of the silica spheres.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Exploring the Diffusion Properties of Pseudomorphic MCM-41 Materials by PFG NMR

1. Introduction Ordered mesoporous silicas such as micelle-templated silicas (MTS) feature unique textural properties in addition to their high surface area: narrow mesopore size distributions, controlled pore size and connectivity make them particularly suitable for chromatographic applications (size exclusion chromatography, HPLC and capillary gas chromatography). In these applications, the p...

متن کامل

Comparative Study between Direct and Pseudomorphic Transformation of Rice Husk Ash into MFI-Type Zeolite.

Pre-shaped mesoporous amorphous rice husk ash (RHA) and MCM-41 derived from RHA as a silica source were transformed into MFI-type zeolites using two different structure-directing agents. Tetrapropylammonium hydroxide (TPAOH) was utilized as an alkali source for silica dissolution and structure control during the direct transformation of RHA into zeolite. A monopropylamine (PA)-containing alkali...

متن کامل

Application of Spherical Mesoporous Silica MCM-41 for Adsorption of Dibenzothiophene (A Sulfur Containing Compound) from Model Oil

Spherical mesoporous silica MCM-41 was synthesized for adsorptive removal of sulfur compounds from fossil fuels using 1mM solution of dibenzothiophene (DBT) in dodecane as model oil. The prepared silica adsorbent has been characterized by nitrogen adsorption-desorption analysis as well as Small Angle X-ray Scattering (SAXS), and transmission and Scanning Electron Microscopy (SEM) methods. R...

متن کامل

Asymmetric Synthesis of Modafinil and its Derivatives by using the Functionalized Silica-based Mesoporous MCM-41

Modafinil [2-[(diphenylmethyl)sulfinyl]acetamide] is used clinically in the treatment of narcolepsy and sleeping disorders. The synthesis of modafinil, begins with the reaction of benzhydrol and thioglycolic acid in trifluoroacetic acid to afford benzhydrylsulfinyl acetic acid. The reaction of acid with thionyl chloride in benzene followed by treatment with ammonium hydroxide gave acetamide...

متن کامل

Effect of Synthesis Conditions on Textural Properties of Silica MCM-41

Several samples of mesoporous silica were prepared via sol-gel chemistry in the presence of CTAB as template with variation of stirring intensity and aging time, ratios of CTAB/SiO2 and NH4OH/H2O in synthesis mixture. Effects of aging temperature, hydrothermal treatment and ter-Butanol addition to the synthesis mixture on the textural properties of obtained samples were also studied. Results of...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 6  شماره 

صفحات  -

تاریخ انتشار 2013