Ultraviolet and visible Raman analysis of thin a-C films grown by filtered cathodic arc deposition

نویسندگان

  • J. Wasyluk
  • T. S. Perova
  • D. W. M. Lau
  • M. B. Taylor
  • D. G. McCulloch
  • J. Stopford
چکیده

Amorphous carbon thin films with a wide range of sp fraction from 20 to 90% grown by filtered cathodic arc deposition have been examined by ultraviolet (UV) at 325 nm and visible Raman spectroscopy at 457 nm excitation wavelength. The comprehensive study of behaviour of G, D and T band with sp/sp content has been carried out. The upwards shift of the G peak with sp content was observed for both excitation wavelengths. It was also found that the I(D)/I(G) ratio decreases with sp content for UV and visible excitations, and for high sp content I(D)/I(G) tends to zero. The dispersion of the G peak is also investigated in this work as a function of sp content. Author for correspondence, tel.: +353 1 896 1432; FAX: +353 1 677 2442; e-mail: [email protected] AC C EP TE D M AN U SC R IP T ACCEPTED MANUSCRIPT

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Deposition and characterization of ultra thin diamond like carbon films

Amorphous hydrogenated and/or nitrogenated carbon films, a-C:H/a-C:N, in overall thickness up to 2 nm are materials of choice as a mechanical and corrosion protection layer of the magnetic media in modern hard disk drive disks. In order to obtain high density and void-free films the sputtering technology has been replaced by different plasma and ion beam deposition techniques. Hydrocarbon gas p...

متن کامل

Effect of the metal concentration on the structural, mechanical and tribological properties of self-organized a-C:Cu hard nanocomposite coatings

The influence of the metal content (0-28 at.%) on the structural, mechanical and tribological properties of a-C:Cu films grown by pulsed filtered cathodic arc deposition is investigated. Silicon and AISI 301 stainless steel have been used as substrate materials. The microstructure, composition and bonding structure have been determined by scanning electron microscopy; combined Rutherford backsc...

متن کامل

Cyclic Voltammetric Behavior of Nitrogen-Doped Tetrahedral Amorphous Carbon Films Deposited by Filtered Cathodic Vacuum Arc

Nitrogen-doped tetrahedral amorphous carbon (ta-C :N) films were deposited by filtered cathodic vacuum arc (FCVA) technique using nitrogen as a background gas. The structure of the ta-C :N films was studied with X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy in terms of nitrogen flow rate used during the film deposition. Potential windows of the films measured in deaerated and un...

متن کامل

Thin films of hard cubic Zr3N4 stabilized by stress.

Hard, refractory thin films consisting of group IVB element mono-nitrides deposited using various chemical and physical vapour-deposition techniques are widely used in wear-resistant applications. As the demand for performance exceeds the capabilities of existing materials, new materials with superior properties must be developed. Here we report the realization and characterization of hard cubi...

متن کامل

ENERGETIC CONDENSATION GROWTH OF MgB2 THIN-FILMS FOR SRF APPLICATIONS*

We report single-step vacuum growth of stoichiometric superconducting thin films of MgB2, using AASC’s cathodic arc deposition process. Energetic condensation using cathodic arcs produces non-equilibrium fast ions (~50-100eV) that allow growth modes on relatively low temperature substrates. We have demonstrated MgB2 films with Tc of 34K by depositing at 275 °C in a single step, from a stoichiom...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2010