An NMR Spectroscopic Investigation of Aluminosilicate Gel in Alkali-Activated Fly Ash in a CO2-Rich Environment
نویسندگان
چکیده
The present study investigated aluminosilicate gel in alkali-activated fly ash exposed to a CO₂-rich environment by means of NMR spectroscopy. The alkali-activated fly ash was exposed to an atmospheric CO₂ concentration of 10% after curing at 80 °C initially for 24 h. Under high concentrations of CO₂, highly reactive components Na and Al, which completely reacted within the first few hours, were unaffected by carbonation, while Si, with relatively slower reactivity, behaved differently. Despite a lower degree of the reaction in the carbonated sample, the monomeric silicates rapidly became of higher polymerization, meaning that exposure to high concentrations of CO₂ caused Si to form a binding gel phase. Consequently, the carbonated sample possessed a higher amount of binding gel. The obtained results may be useful to understand the fundamental chemistry and behavior of aluminosilicate gel under high concentrations of CO₂.
منابع مشابه
Microstructural and Mechanical Properties of Alkali Activated Colombian Raw Materials
Microstructural and mechanical properties of alkali activated binders based on blends of Colombian granulated blast furnace slag (GBFS) and fly ash (FA) were investigated. The synthesis of alkali activated binders was conducted at 85 °C for 24 h with different slag/fly ash ratios (100:0, 80:20, 60:40, 40:60, 20:80, and 0:100). Mineralogical and microstructural characterization was carried out b...
متن کاملMicrostructural Characteristics of Geopolymers Based on Alkali-Activated Fly Ash
Aluminosilicate geopolymers with a high silica molar ratio have been prepared by mixing Croatian coal-ash (ASTM Class F) and sodium silicate solution (water glass, technical grade). The samples were cured at 85 °C for 8 h and 24 h in different experimental conditions. Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM/EDS) have been use...
متن کاملOne-part geopolymer mixes from geothermal silica and sodium aluminate
At present, the most commonly used building material is ordinary Portland cement (OPC). However, OPC has a negative environmental effect during synthesis, with the release of significant amount of CO2 greenhouse gas. The cement industry is responsible for 5-8% of total global anthropogenic CO2 emissions. Geopolymerization is a technology capable of turning industrial wastes into strong and chem...
متن کاملIdentifying Glass Compositions in Fly Ash
In this study, four Class F fly ashes were studied with a scanning electron microscope; the glassy phases were identified and their compositions quantified using point compositional analysis with k-means clustering and multispectral image analysis. The results showed that while the bulk oxide contents of the fly ashes were different, the four fly ashes had somewhat similar glassy phase composit...
متن کامل