Room Temperature Solid State Synthesis, Characterization, and Application of a Zinc Complex with Pyromellitic Acid
نویسندگان
چکیده
The complex [Zn2(btca)(H2O)4] was synthesized with 1,2,4,5-benzenetetracarboxylic acid (H4btca) and zinc acetate as materials via a room-temperature solid state reaction. The composition and structure of the complex were characterized by elemental analyses (EA), Fourier transform infrared spectroscopy (FTIR), X-ray powder diffraction (XRD), and thermogravimetric (TG) analysis. The index results of X-ray powder diffraction data showed that the crystal structure of the complex belonged to monoclinic system with cell parameters a = 9.882 Å, b = 21.311 Å, c = 15.746 Å, and β = 100.69◦. In order to expand the application of the complex, the nanometer zinc oxide was prepared by using the complex as a precursor, and the effect of the thermal decomposition temperature on the preparation of the nanometer zinc oxide was studied. The results showed that the grain size of zinc oxide gradually grew with the increase of the pyrolysis temperature, the obtained nanometer zinc oxide was spherical, and the diameter of the particles was about 25 nm.
منابع مشابه
Preparation of Nickel Nanoparticles by Intramolecular Reaction of Nickel(II) Hydrazine Complex in the Solid State at Room Temperature
Ni6(N2H4)6(SO4)4(OH)2(H2O)8](SO4)(H2O)10 complex was prepared according to literature report. The reaction between aforementioned complex via sodium alkoxides as a reactants, were carried out in the solid state. The [Ni6(N2H4)6(SO4)4(OH)2(H2O)8](SO4)(H2O)10 undergoes an intramolecular two electrons oxidation-reduction reaction at room temperature and metallic nickel nanoparticles (Ni1-Ni5) was ...
متن کاملCobalt oxide nanoparticles by solid-state thermal decomposition: Synthesis and characterization
In this study, mononuclear octahedral cobalt(III) Schiff base complex [CoL3], L = (5-bromo-2-hydroxybenzyl-2-furylmethyl)imine, was synthesized from the reaction of Co(NO3)2•6H2O and the Schiff base ligand L in methanol as solvent. It used as a new precursor to prepare spinel type cobalt oxide nanoparticles by a facile solid-state thermal decomposition. Controlling the temperature and time, Co3...
متن کاملSolid–Solid Synthesis, Crystal Structure and Thermal Decomposition of Copper(II) Complex of 2-Picolinic Acid
The copper(II) complex [Cu(pic)2]·2H2O was synthesized with 2-picolinic acid (Hpic) and copper acetate as reactants by room temperature solid-solid reaction. The composition and structure of the complex was characterized by elemental analyses, single crystal X-ray diffraction, X-ray powder diffraction, FT-IR spectroscopy and thermogravimetry-differential scanning calor...
متن کاملPreparation of ZnO Nanocrystals with Desired Morphology from Coordination Polymers through a Solid-state Decomposition Route
One-dimensional (1D) coordination polymer, [Zn(4,4´-bpy)(H2O)4](ADC).4H2O (1) (4,4´-bpy = 4,4´-bipyridine and H2ADC = acetylenedicarboxylic acid), and three-dimensional (3D) metal-organic framework (MOF), Zn(ADC)2.(HTEA)2(2) (HTEA = triethylamine) were prepared at room temperature. The compounds were characterized by single-crystal X-ray diffraction and powder X-ray diffraction (PXRD) analyses....
متن کاملSynthesis and characterization of transition metal doped ZnSe/ZnS nanocrystals by a rapid photochemical method
In the present work, a one pot, rapid and room temperature photochemical Synthesis of transition metal (TM; Cu, Mn, Cr)-doped ZnSe/ZnS core/shell nanocrystals (NCs) was reported. FT-IR spectrum confirmed the capping of ZnSe by thioglycolic acid. XRD and TEM analysis demonstrated zinc blende phase NCs with an average size of around 3 and 5 nm for TM:ZnSe and TM:ZnSe/ZnS NCs, respectively. PL spe...
متن کامل