Microstructure of Spark Plasma-Sintered Silicon Nitride Ceramics
نویسندگان
چکیده
The microstructure and phase composition of the high-content Al2O3-Y2O3-doped spark plasma-sintered silicon nitride were investigated. Fully dense silicon nitride ceramics with a typical α-Si3N4 equiaxed structure with average grain size from 200 to 530 nm, high elastic modulus of 288 GPa, and high hardness of 2038 HV were spark plasma sintered (SPSed) at 1550 °C. Silicon nitride with elongated β-Si3N4 grains, higher hardness of 1800 HV, density of 3.25 g/cm3, and Young's modulus 300 GPa SPSed at 1650 °C was also reviewed.
منابع مشابه
Microstructure of spark plasma sintered TiB2 and TiB2–AlN ceramics
In this research study, the effects of aluminum nitride (AlN) additive on the densification behavior and microstructure development of titanium diboride (TiB2) based ceramic matrix composite were investigated. In this way, a monolithic TiB2 ceramic and a TiB2–5 wt% AlN ultrahigh temperature ceramic composite were fabricated by spark plasma sintering (SPS) proces...
متن کاملMicrostructure and Phase Composition of Cold Isostatically Pressed and Pressureless Sintered Silicon Nitride.
The microstructure and physical properties of new Y2O3 and Al2O3 oxide-doped silicon nitride ceramics fabricated by cold isostatic pressing and free sintering were investigated. The phase composition of produced material was also studied by X-ray diffraction at room and elevated temperature. The fabricated ceramics featured a microstructure of Si5AlON7 grains with a fine-grained α-Si3N4 with a ...
متن کاملStructural and Electrical Characterization of Sintered Silicon Nitride Ceramic
The electrical conduction phenomena, dielectric response and microstructure have been discussed in sintered silicon nitride ceramics at different temperature and frequencies. Microstructure and phase of the sintered samples was investigated by Scanning Electron Microscope (SEM) and X-ray diffractometer (XRD). The electrical conductivity, dielectric constant and dielectric loss increases exponen...
متن کاملSolid state sintering of very low and negative thermal expansion ceramics by Spark Plasma
Lithium aluminosilicate powder precursors of compositions Li2O:Al2O3:SiO2 as 1:1:2; and 1:1:3.11 were synthesized and sintered by the Spark Plasma Sintering technique. The sintering conditions were adjusted to obtain dense ceramic materials in an attempt to avoid the presence of a glassy phase. XRD and SEM images were employed for composition and microstructure characterization. The coefficient...
متن کاملInvestigation of the Physical and Mechanical Properties of Silicon Carbide Prepared on an Industrial Scale
In this study, an industrial polycrystalline SiC tile was successfully sintered by pressureless sintering at 2150°C for 1 hour. The physical and mechanical properties of silicon carbide including density, hardness, bending strength, and fracture toughness were evaluated. The results indicated that the mentioned properties were 3.08 g.cm-3, 2503 HV0, 249.3 MPa, and 1.23 MPam0.5</...