Performance of Flame Retardant Wool Fabric Grafted with Vinyl Phosphate
نویسندگان
چکیده
In this paper, a flame retardant dimethyl-2-(methacryloyloxyethyl) phosphate (DMMEP) was applied to wool fabrics by the graft copolymerization technique initiated with potassium persulfate (KPS) in water media. FTIR and SEM testing were used to explore the grafting evidence on the fiber surface, the SEM results show chemical deposition on the wool fiber surface and the scales could not be seen clearly. FTIR testing exhibited IR absorption of DMMEP on the wool fiber. Thermal gravimetric analysis, differential thermal analysis (DTA), and char residue morphology SEM observation show the decomposition mode of wool fabrics and infer the possible flame retardant mechanism. The phosphorus based flame retardant DMMEP was prone to promote more nonflammble char during combustion, and increased add-on of DMMEP produced increased fabric char. With a DMMEP add-on increase from 50% to 100% on the weight of wool fabric, the treated wool fabric demonstrated high flame retardancy with an LOI above 35% which means it can not be ignited with a candle like fire, and could pass the vertical flammability test. DMMEP treatment slightly affected whiteness and moisture regain, but yielded a relatively large decrease in permeability and tensile strength, which should be explored further in later research.
منابع مشابه
Flame Retardant Applications in Camping Tents and Potential Exposure
Concern has mounted over health effects caused by exposure to flame retardant additives used in consumer products. Significant research efforts have focused particularly on exposure to polybrominated diphenyl ethers (PBDEs) used in furniture and electronic applications. However, little attention has focused on applications in textiles, particularly textiles meeting a flammability standard known...
متن کاملApplication of Oligomers with Urea Linkage as Flame Retardant and Antibacterial Materials in Jute Fabric
متن کامل
Heat Release Property and Fire Performance of the Nomex/Cotton Blend Fabric Treated with a Nonformaldehyde Organophosphorus System
Blending Nomex® with cotton improves its affordability and serviceability. Because cotton is a highly flammable fiber, Nomex®/cotton blend fabrics containing more than 20% cotton require flame-retardant treatment. In this research, combination of a hydroxyl functional organophosphorus oligmer (HFPO) and 1,2,3,4-butanetetracarboxylic acid (BTCA) was used for flame retardant finishing of the 65/3...
متن کاملA Fast Method for Synthesis Magnesium Hydroxide Nanoparticles, Thermal Stable and Flame Retardant Poly vinyl alcohol Nanocomposite
Magnesium hydroxide nanostructures as an effective flame retardant were synthesized by a facile and rapid microwave reaction. The effect of different surfactants such as cationic, anionic and polymeric on the morphology of magnesium hydroxide nanostructures was investigated. Nanostructures were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform in...
متن کاملHydrothermal Synthesis of Nickel Hydroxide Nanostructures and Flame Retardant Poly Vinyl Alcohol and Cellulose Acetate Nanocomposites
Nickel hydroxide nanostructures were synthesized by a hydrothermal reaction. The effect of different precursors and surfactants on the morphology of nickel hydroxide nanostructures was investigated. Nanostructures were characterized by X-ray diffraction, energy dispersive X-ray spectroscopy, scanning electron microscopy and Fourier transform infrared spectroscopy. The influence of Ni(OH)2 nano...
متن کامل